Lubricating Compositions

ABSTRACT

A lubricating composition suited to use for lubricating a hydraulic system includes an oil of lubricating viscosity and a compound comprising a polyolefin-substituted bridged hydroxyaromatic compound or metal salt thereof, wherein the wherein the polyolefin is derived from a isobutylene having a number average molecular weight of 150 to 800.

BACKGROUND

The invention relates generally to lubricating compositions (lubricants) and finds particular application in connection with an additive for a lubricating composition and to a lubricating method.

Phenol-based detergents are known. Among these are phenates based on phenolic monomers linked with sulfur bridges or alkylene bridges such as methylene linkages derived from formaldehyde. The phenolic monomers themselves are typically substituted with an aliphatic hydrocarbyl group to provide a measure of oil solubility. The hydrocarbyl groups may be alkyl groups, such as dodecylphenol (or propylene tetramer-substituted phenol). Basic sulfurized polyvalent metal phenates are described, for example, in U.S. Pat. No. 2,680,096, to Walker et al., issued Jun. 1, 1954; and U.S. Pat. No. 3,372,116, to Meinhardt, issued Mar. 6, 1968.

Recently, however, certain alkylphenols and products prepared from them have come under increased scrutiny due to their classification as potentially harmful materials. In particular, alkylphenol detergents which are based on oligomers of C₁₂ alkyl phenols may contain residual monomeric C₁₂ alkyl phenol species. These detergents include those derived from para-dodecyl phenol. There is interest, therefore, in developing alkyl-substituted phenate detergents, for uses in lubricants, fuels, and as industrial additives, which reduce or eliminate the need for dodecylphenol-based compounds.

There have been several efforts to prepare phenate detergents that do not contain C₁₂ alkyl phenols. U.S. Pat. No. 7,435,709, to Stonebraker, et al., issued Oct. 14, 2008, discloses a linear alkylphenol-derived detergent which is a salt of a reaction product of an olefin having at least 10 carbon atoms and a hydroxyaromatic compound. Greater than 90 mole % of the olefin is a linear C₂₀-C₃₀ n-alpha olefin, less than 10 mole % of the olefin is a linear olefin of less than 20 carbon atoms, and less than 5 mole % of the olefin is a branched chain olefin of 18 carbons or less.

U.S. Pub. No. 2011/0190185, to Sinquin, et al, published Aug. 4, 2011, discloses an overbased salt of an oligomerized alkylhydroxyaromatic compound. The alkyl group is derived from an olefin mixture comprising propylene oligomers having an initial boiling point of at least 195° C. and a final boiling point of greater than 325° C. The propylene oligomers may contain a distribution of carbon atoms that include at least 50 wt. % C₁₄ to C₂₀ carbon atoms.

U.S. Pub. No. 2011/0124539, to Sinquin, et al, published May 26, 2011, discloses an overbased, sulfurized salt of an alkylated hydroxyaromatic compound. The alkyl substituent is a residue of at least one isomerized olefin having from 15 to 99 wt. % branching. The hydroxyaromatic compound may be a phenol, cresol, xylenol, or mixture thereof.

U.S. Pub. No. 2011/0118160, to Campbell, et al., published May 19, 2011, discloses an alkylated hydroxyaromatic compound prepared by reacting a hydroxyaromatic compound with at least one branched olefinic propylene oligomer having from 20 to 80 carbon atoms. Suitable hydroxyaromatic compounds include phenol, catechol, resorcinol, hydroquinone, pyrogallol, cresol, and the like.

U.S. Pub. No. 2010/0029529, to Campbell, et al., published Feb. 4, 2010, discloses an overbased salt of an oligomerized alkylhydroxyaromatic compound. The alkyl group is derived from an olefin mixture comprising propylene oligomers having an initial boiling point of at least 195° C. and a final boiling point of no more than 325° C.

U.S. Pub. No. 2008/0269351, to Campbell, et al., published Oct. 30, 2008, discloses an alkylated hydroxyaromatic compound prepared by reacting a hydroxyaromatic compound with a branched olefinic oligomer having from 20 to 80 carbon atoms.

U.S. Pat. No. 6,310,009, to Carrick, et al., issued Oct. 30, 2001, discloses bridged phenolic compounds, each phenol group being substituted with an alkyl group of 1 to 60 carbon atoms, e.g., 9 to 18 carbon atoms.

There remains a need for a phenolic material with appropriate oil solubility, viscosity performance, and detergency (characteristic of moderate chain length alkyl groups) but free from or substantially free from C₁₂ alkyl phenol moieties.

BRIEF DESCRIPTION

In accordance with one aspect of the exemplary embodiment, a lubricating composition includes an oil of lubricating viscosity and a compound containing a polyolefin-substituted bridged hydroxyaromatic compound or metal salt thereof.

In accordance with another aspect of the exemplary embodiment, a method of lubricating a mechanical device with the lubricating composition is disclosed.

In accordance with another aspect of the exemplary embodiment, a method of forming a lubricating composition including an oil of lubricating viscosity and a compound containing a polyolefin-substituted bridged hydroxyaromatic compound or metal salt thereof is described.

In accordance with another aspect, a use of the composition for lubricating a mechanical device is also disclosed.

DETAILED DESCRIPTION

Aspects of the exemplary embodiment relate to a lubricating composition, method of use and method of manufacturing the composition. The lubricating composition contains an oil of lubricating viscosity and a polyolefin-substituted bridged hydroxyaromatic compound or salt thereof.

The exemplary compounds described herein are bridged polyolefin-substituted hydroxyaromatic (e.g., phenol) compounds and their salts. The compounds are free from or substantially free from unsubstituted phenol moieties. Such compounds and their salts are useful as lubricant additives.

Suitable hydroxyaromatic compounds include phenol, catechol, resorcinol, hydroquinone, pyrogallol, cresol, and the like. In one embodiment, the hydroxyaromatic compounds that are bridged include no more than one aromatic ring.

The term “substantially free” as it refers to the exemplary compound, means that less than 0.01 mol. %, or less than 0.001 mol. %, or less than 0.0001 mol. % of the exemplary polyolefin-substituted bridged hydroxyaromatic compound in the lubricating composition is substituted with one or more C₁₂ alkyl groups. In one embodiment, the lubricating compound contains less than 0.5 wt. %, or less than 0.1 wt. %, or less than 0.01 wt. %, or less than 0.001 wt. %, of C₁₂ alkyl hydroxyaromatic compounds.

The lubricating composition may also include a bridged phenate. In the exemplary embodiment, the compound is not coupled with cresol. The compound can serve as a dispersant or detergent in the lubricating composition.

A. The Polyolefin-Substituted Bridged Hydroxyaromatic Compound

The exemplary polyolefin-substituted, bridged hydroxyaromatic compound is a bridged phenol in which at least one hydroxyl group is directly bonded to an aromatic ring that is substituted with a polyolefin group.

The aromatic polyol on which the exemplary compound is based may be a substituted or unsubstituted compound that has at least one hydroxyl group directly bonded to an aromatic group (within the definition of Hückel Rule 4π+2 electrons) such as phenol. An exemplary polyolefin-substituted aromatic polyol compound may be represented by the general structure shown in Formula I:

and salts thereof,

where each R¹ and each R² represents a polyolefin group,

X represents a bridging group, such as a sulfur or an alkylene bridging group containing 1 to 8 carbon atoms (e.g., a bridge derived from one or more aldehyde and/or propanal monomer units);

Y and Z each represent a terminal group, such as —H, —OH, a C₁-C₆ alkyl group, or a group derived from the bridging monomer (e.g., —SH, an aldehyde-derived group, such as —C(H)═O, or the like);

each n is at least 1, such as up to 3, on average, or up to 2, or 1;

m is at least 1, such as up to 5, or up to 4, or up to 3, on average, such as 1 or 2; and

p is at least 1, such as up to 5, on average, or 1 or 2.

An exemplary salt may be represented by the general structure shown in Formula II:

where M represents a cation which is linked to at least one of the O⁻ groups; and x is at least 1, such as 2 in the case of a calcium ion.

The exemplary compound of Formula II may also be associated with a counter ion in the compound. For example, in an overbased compound, the metal ion to compound ratio may be raised above the stoichiometric amount, e.g., by bubbling CO₂ through the mixture to provide a carbonate counterion. As will be appreciated, these aspects can also be used in combinations thereof.

Examples of branched polyolefin groups suitable for use as R¹ and R² include polyolefin groups which are derived from a branched alkene having at least 4 carbon atoms, or up to 12 carbon atoms, or up to 8 carbon atoms, or up to 6 carbon atoms, such as a C₄-C₆ branched alkene. Suitable branched alkenes include isobutylene (2-methylpropene), 2-methylbutene, 2-ethyl-1-butene, 2-methyl-1-pentene, 3-methyl-1-pentene, 4-methyl-1-pentene, 2-methyl, 3-methyl-1-pentene, 2-ethyl-1-pentene, 3-ethyl-1-pentene, 2-methyl-1-hexene, 3-methyl-1-hexene, 2-ethyl-1-hexene, 3-ethyl-1-hexene, 4-ethyl-1-hexene, 2-methyl-1-heptene, 3-methyl-1-heptene, 2-methyl-1-octene, 2-methyl-1-nonene, 2-methyl-1-decene, 2-methyl-1-undecene, and mixtures thereof. Each polyolefin group is derived from at least two or at least three, or at least four, or up to twenty, or up to eighteen, or up to twelve branched alkene monomer units to form a chain with at least two or at least three, or at least four branches from the main chain. In one embodiment, the polyolefin includes a chain derived from at least four, or at least five, or up to eighteen, or up to eight, or up to seven, or up to six branched alkene units. The branched alkene may be branched at the alpha or beta position, or further along the longest chain. In one embodiment, at least one or both of R¹ and R² are derived from a branched alkene which is solely or at least partially isobutylene and at least one or both of R¹ and R² is/are each polyisobutylene (PIB).

R¹ and R² may be independently a polyolefin of 8 to 50 carbon atoms, or at least 10 carbon atoms, or at least 12 carbon atoms, or at least 14 carbon atoms, or at least 16 carbon atoms, or at least 18 carbon atoms, or at least 20 carbon atoms, or at least 24 carbon atoms, or up to 40 carbon atoms, or up to 35 carbon atoms, or up to 30 carbon atoms.

The polyolefin group may have a number-average molecular weight M_(n) of at least 150, or at least 200, or at least 300, or up to 800, or up to 600, or up to 500, or up to 400, or up to 360. In some embodiments R₁ and R₂ may have different chain lengths. In the exemplary embodiment, R₁ and R₂ are of the same chain length (or have the same number of branches off the main chain or differ by no more than ±1 branch). A polyolefin group with M_(n) of less than 500, e.g., up to about 400 is particularly suitable as it allows the compound to provide good detergent properties for deposit control and cleanliness without resulting in viscosity creep or undesirable thickening of the oil.

In one embodiment, the compound may be a mixture of polyolefin-substituted, bridged hydroxyaromatic compounds with high and low molecular weight polyolefin groups, respectively. The low molecular weight polyolefin may be up to a C₃₀ or up to a C₂₅ polyolefin. The high molecular weight polyolefin may be up to a C₄₀ or up to a C₃₅ polyolefin. A ratio of the compound with low molecular weight polyolefin to the compound with high molecular weight polyolefin may be at least 50:50 by weight, or at least 80:20, or at least 90:10.

In one embodiment, the compound is free of C₈ and higher unbranched alkyl groups.

In one embodiment, R₁ and R₂ are each composed solely of carbon and hydrogen.

In one embodiment, the compound consists solely of elements selected from the group consisting of C, H, O, S and the counterion(s).

The compound may have a weight average molecular weight Mw of at least 550, or at least 700, or at least 750, or at least 800 in its unsalted form. The weight average molecular weight of the compound may be up to 5600, or up to 2800, or up to 1200, or up to 1000, or up to 950, in its unsalted form.

In one embodiment X is an alkylene, e.g., a methylene bridge, or a sulfur bridge. In the case of an alkylene bridge, the bridge may be up to 4 carbons in length, or up to 3 carbons in length.

As will be appreciated, these aspects can also be used in combinations thereof.

The salt of the compound of Formula I may be formed by reacting a cation or source of the cation with the compound. The compound of Formula I thus serves as the anion (or “substrate”) in the salt. The cation or source thereof reacts with one or more of the residual OH groups to form a neutral or overbased salt of the above-described coupled polyolefin-substituted aromatic polyol.

In one embodiment, the cation is a metallic cation. The metallic cation may be derived from an alkaline earth metal, such as calcium, barium or magnesium (typically calcium), or an alkali metal, such as sodium or potassium (typically sodium). The metal cation may have an atomic weight of at least 6 or at least 12.

Exemplary metal cations include alkali metal cations, alkaline earth metal cations, transition metal cations, and combinations thereof. Examples of metal cations include Li⁺, Na⁺, K⁺, Rb⁺, Cs⁺, Be²⁺, Mg²⁺, Ca²⁺, Sr²⁺, Ba²⁺, Sc³⁺, Sc²⁺, Sc⁺, Y³⁺, Y²⁺, Y⁺, Ti⁴⁺, Ti³⁺, Ti²⁺, Zr⁴⁺, Zr³⁺, Zr²⁺, Hf⁴⁺, Hf³⁺, V⁴⁺, V³⁺, V²⁺, Nb⁴⁺, Nb³⁺, Nb²⁺, Ta⁴⁺, Ta³⁺, Ta²⁺, Cr⁴⁺, Cr³⁺, Cr²⁺, Cr⁺, Mo⁴⁺, Mo³⁺, Mo²⁺, Mo⁺, W⁴⁺, W³⁺, W²⁺, W⁺, Mn⁴⁺, Mn³⁺, Mn²⁺, Mn⁺, Re⁴⁺, Re³⁺, Re²⁺, Re⁺, Fe⁶⁺, Fe⁴⁺, Fe³⁺, Fe²⁺, Fe⁺, Ru⁴⁺, Ru³⁺, Ru²⁺, Os⁴⁺, Os³⁺, Os²⁺, Os⁺, Co⁵⁺, Co⁴⁺, Co³⁺, CO²⁺, Co⁺, Rh⁴⁺, Ru³⁺, Rh²⁺, Rh⁺, Ir⁴⁺, Ir³⁺, Ir²⁺, Ir⁺, Ni³⁺, Ni²⁺, Ni⁺, Pd⁴⁺, Pd²⁺, Pd⁺, Pt⁴⁺, Pt³⁺, Pt²⁺, Pt⁺, Cu⁴⁺, Cu³⁺, Cu²⁺, Cu⁺, Ag³⁺, Ag²⁺, Ag⁺, Au⁴⁺, Au³⁺, Au²⁺, Au⁺, Zn²⁺, Zn⁺, Cd²⁺, Cd⁺, Hg⁴⁺, Hg²⁺, Hg⁺, Al³⁺, Al²⁺, Al⁺, Ga³⁺, Ga⁺, In³⁺, In²⁺, Tl³⁺, Tl⁺, Si⁴⁺, Si³⁺, Si²⁺, Si⁺, Ge⁴⁺, Ge³⁺, Ge²⁺, Ge⁺, Sn⁴⁺, Sn²⁺, Pb⁴⁺, Pb²⁺, As³⁺, As²⁺, As⁺, Sb³⁺, Bi³⁺, Te⁴⁺, Te²⁺, La³⁺, La²⁺, Ce⁴⁺, Ce³⁺, Ce²⁺, Pr⁴⁺, Pr³⁺, Pr²⁺, Nd³⁺, Nd²⁺, Sm³⁺, Sm²⁺, Eu³⁺, Eu²⁺, Gd³⁺, Gd²⁺, Gd⁺, Tb⁴⁺, Tb³⁺, Tb²⁺, Tb⁺, Db³⁺, Db⁺⁺, Ho³⁺, Er³⁺, Tm⁴⁺, Tm³⁺, Tm²⁺, Yb³⁺, Yb²⁺, and Lu³⁺. Particularly useful are those which form stable salts, i.e., which do not decompose by more than a minor amount over the expected lifetime and operating conditions of the lubricating composition.

In one embodiment, the metallic cation is derived from a metal base such as a metal base of a hydroxide, an oxide, carbonate, or bicarbonate. The metal base may be a hydroxide or an oxide. For example the metallic cation may be derived from calcium hydroxide, calcium oxide, sodium hydroxide, sodium oxide, magnesium hydroxide, magnesium oxide, or mixture thereof.

In one embodiment, the cation is an ash-free cation. An ash-free (ashless) organic cation is an organic ion that does not contain ash-forming metals. In one embodiment, the compound in the salt form has a sulfated ash of up to 0.5 wt. %, or up to 0.4 wt. %, according to ASTM D874.

In one embodiment, the cation is a pnictogen cation. As used herein the term “pnictogens” includes the elements in column 15 of the periodic table. The non-metallic pnictogens include nitrogen and phosphorus (typically nitrogen). The pnictogen cation may be derived from a source of the cation containing a primary amine, a secondary amine, a tertiary amine, or mixture thereof. In one embodiment, the amine salt may be derived from a secondary or tertiary amine.

When the cation is pnictogen cation derived from an amine or ammonium compound, the pnictogen cation (or the amine from which it is derived) may have molecular weight of at least 260 g/mol, or at least 300 g/mol or at least 350 g/mol, or at least 500 g/mol.

The pnictogen cation may be derived from a mono-, di-, or tri-substituted amine. Specific examples include primary alkylamines, such as methylamine, ethylamine, n-propylamine, n-butylamine, n-hexylamine, n-octylamine, 2-ethylhexylamine, benzylamine, 2-phenylethylamine, cocoamine, oleylamine, and tridecylamine (CAS #86089-17-0); secondary and tertiary alkylamines such as isopropylamine, sec-butylamine, t-butylamine, cyclopentylamine, cyclohexylamine, and 1-phenylethylamine; dialkylamines, such as dimethylamine, diethylamine, dipropylamine, diisopropylamine, dibutylamine, dicyclohexylamine, di-(2-ethylhexyl)amine, dihexylamine, ethylbutylamine, N-ethylcyclohexylamine, and N-methylcyclohexylamine; cycloalkylamines, such as piperidine, N-ethylpiperidine, N,N′-dimethylpiperazine, morpholine, N-methylmorpholine, N-ethylmorpholine, N-methylpiperidine, pyrrolidine, N-methylpyrrolidine, and N-ethylpyrrolidine; and trialkylamines, such as trimethylamine, triethylamine, tripropylamine, triisopropylamine, tri-n-butylamine, trihexylamine, N,N-dimethylbenzylamine, dimethylethylamine, dimethylisopropylamine, dimethylbutylamine, and N,N-dimethylcyclohexylamine.

When the pnictogen cation includes at least one hydrocarbyl group (a quaternary ammonium ion), the pnictogen cation may be an ashless organic cation. Example ammonium cations of this type include N-substituted long chain alkenyl succinimides and aliphatic polyamines. N-substituted long chain alkenyl succinimides useful herein may be derived from an aliphatic polyamine, or mixture thereof. The aliphatic polyamine may be aliphatic polyamine such as an ethylenepolyamine, a propylenepolyamine, a butylenepolyamine, or mixture thereof. Examples of N-substituted long chain alkenyl succinimides include polyisobutylene succinimide with number average molecular weight of the polyisobutylene substituent of at least 350, or at least 500, or at least 550, or at least 750, and can be up to 5000, or up to 3000, or up to 2500. Such succinimides can be formed, for example, from high vinylidene polyisobutylene and maleic anhydride.

Example N-substituted long chain alkenyl succinimides useful herein as pnictogen cations include those derived from succinimide dispersants, which are more fully described in U.S. Pat. Nos. 3,172,892, 3,219,666, 3,316,177, 3,340,281, 3,351,552, 3,381,022, 3,433,744, 3,444,170, 3,467,668, 3,501,405, 3,542,680, 3,576,743, 3,632,511, 4,234,435, RE 26,433, 6,165,235, 7,238,650, and EP Patent Application 0 355 895 A.

Example aliphatic polyamines useful as the pnictogen cation include ethylenepolyamines, propylenepolyamines, butylenepolyamines, and mixtures thereof. Example ethylenepolyamines include ethylenediamine, diethylenetriamine, triethylenetetramine, tetraethylenepentamine, pentaethylene-hexamine, polyamine still bottoms, and mixtures thereof.

In one embodiment, the exemplary polyolefin-substituted bridged hydroxyaromatic compound salt may be overbased, i.e., contain an excess of the metal cation in relation to the number of hydroxyl groups present in the compound. There are two common measures of basicity that are commonly used in the field of lubricant additives: Total Base Number (TBN), as measured by ASTM D2896, is a titration that measures both strong and weak bases, while ASTM D4739-11 “Standard Test Method for Base Number Determination by Potentiometric Hydrochloric Acid Titration,” (BN) is a titration that measures strong bases but does not readily titrate weak bases, such as certain amines. TBN and BN are expressed as an equivalent in milligrams of potash per gram of oil (mg of KOH/g).

Total base number (TBN), as used herein, is the quantity of acid, expressed in terms of the equivalent number of milligrams of potassium hydroxide (meq KOH), that is required to neutralize all basic constituents present in 1 gram of a sample of the lubricating oil. The TBN values reported herein are determined according to ASTM Standard D2896-15, “Standard Test Method for Base Number of Petroleum Products by Potentiometric Perchloric Acid Titration” (2015), ASTM International, West Conshohocken, Pa., 2003 (hereinafter, “D2896”). In various aspects, the neutral salt compound has a TBN of at least 50 mg of KOH/g, or at least 60 mg of KOH/g on an oil-free basis. The TBN of the neutral salt may be up to 300 mg KOH/g, or up to 250 mg KOH/g, or up to 165 mg KOH/g, on an oil-free basis. In various aspects, the lubricating composition containing the compound has a TBN of at least 3 mg KOH/g, or at least 4 mg of KOH/g, or at least 6 mg of KOH/g.

The cation may serve as a basic component of the lubricating composition which, in combination with any other basic components of the lubricating composition, may provide the lubricating composition with a TBN of at least 5, or at least 8, or at least 10, or at least 15, or at least 25. The cation itself may have a TBN of at least 10 or at least or at least 15, or at least 25, or at least 50.

B. Method of Forming the Polyolefin-Substituted Bridged Hydroxyaromatic Compound

A bridged (e.g., sulfur-coupled or formaldehyde-coupled) polyolefin-substituted hydroxyaromatic compound of Formula I or II may be formed through well-known techniques.

In one embodiment, the salt of a polyolefin-substituted hydroxyaromatic compound may be obtained/obtainable by (i) reacting a hydroxy aromatic compound (e.g., phenol) with an branched alkene, such as isobutylene, optionally in the presence of a catalyst, to form a hydroxy-substituted intermediate compound, (ii) coupling the intermediate compound, e.g., with sulfur or formaldehyde, and (to form the salt) iii) reacting the bridged compound formed in step (ii) with a metal base or a pnictogen base.

(i) Formation of Polyisoalkylene-Substituted Phenol Compound

The intermediate compound may be formed by reaction of a phenol with a poly(branched alkene). Substitution occurs primarily at the para position, although minor amounts of ortho- and/or meta-substitution may occur. The ratio of poly(branched alkene) to phenol may be from 1:1 to 1:6, such as at least 1:2. An excess of phenol helps to ensure primarily mono-substitution of the poly(branched alkene).

For example, a polyisobutylene-substituted phenol:

where q is, for example, from 5 to 10, or up to 7, or at least 6, on average, may be formed by reacting phenol with a polyolefin (e.g., polyisobutylene), optionally in the presence of a base catalyst. Typically the reaction occurs in the presence of a base catalyst.

Example catalysts include Lewis acid catalysts, solid acid catalysts, trifluoromethanesulfonic acid, and acidic molecular sieve catalysts. Suitable Lewis acid catalysts include aluminum trichloride, aluminum tribromide, aluminum triiodide, boron trifluoride, boron tribromide, boron triiodide and the like. Suitable solid acidic catalysts include zeolites, acid clays, and/or silica-alumina.

Reaction Scheme 1 illustrates the reaction:

where b is for example, from 4-10.

The process to prepare the intermediate may be carried out a reaction temperature of 1° C. to 52° C., or 5° C. to 20° C., or 10° C. to 15° C. The formation of the intermediate may be performed in the presence or absence of solvent. The solvent may include a hydrocarbon such as hexane, toluene, xylene, diluent oil, cyclohexane, or mixture thereof. In one embodiment the process to prepare the intermediate is performed in the presence of a solvent. Optionally the solvent is removed before sulfurizing and/or reacting of the intermediate with the metal base. The reaction mixture may then be neutralized with calcium hydroxide, followed by addition of diatomaceous earth and ammonia hydroxide to remove residual catalyst. The reaction mixture is filtered and the filtrate heated under vacuum to remove volatiles by distillation.

ii) Coupling the Intermediate Compound with Sulfur or Aldehyde and Formation of Salt

Sulfurization may be performed by contacting the intermediate compound with a sulfur source which introduces S_(x) bridging groups between the polyolefin-substituted phenol compound in the presence of a base. Reaction Scheme 2 illustrates the reaction.

where x is from 1-5, on average, such as up to 3, or up to 2, on average.

Any suitable sulfur source can be used such as, for example, elemental sulfur or a halide thereof such as sulfur monochloride, sulfur dichloride, hydrogen sulfide, sulfur dioxide, or a sodium sulfide hydrate. The sulfur can be employed either as molten sulfur or as a solid (e.g., powder or particulate) or as a solid suspension in a compatible hydrocarbon liquid, such as ethylene glycol.

Sulfur may be employed at from 0.5 to 4 moles per mole of the intermediate compound in the reaction system. In one embodiment, sulfur is employed at from 0.8 to 2 moles per mole of the intermediate compound.

The temperature range in which the sulfurization reaction is carried out is generally 80-250° C., e.g., 100-220° C. The reaction can be conducted under atmospheric pressure (or slightly lower) or at elevated pressures. During sulfurization a significant amount of by-product hydrogen sulfide gas is evolved. In one embodiment the reaction is carried out under vacuum to facilitate the H₂S elimination.

Other sulfurization techniques which may be adapted to use herein are described, for example, in U.S. Pat. No. 2,680,096, to Walker et al., issued Jun. 1, 1954; U.S. Pat. No. 3,372,116, to Meinhardt, issued Mar. 6, 1968; U.S. Pat. No. 3,036,971, to Otto, issued May 29, 1962, U.S. Pat. No. 7,435,709, to Stonebraker, et al., issued Oct. 14, 2008, U.S. Pat. No. 8,772,209 to Mahieux, et al., issued Jul. 8, 2014, U.S. Pat. No. 9,062,271 to Jukes, et al., issued Jun. 23, 2015, and U.S. Pub. No. U.S. Pub. No. 20150045269, published Feb. 12, 2015, to Walker, et al. The 20150045269 publication, for example, describes preparation of a sulfurized alkaline earth metal (e.g., calcium) dodecylphenate by reacting dodecylphenol with calcium hydroxide or calcium oxide and an alkylene glycol. The reaction product is reacted with sulfur.

The sulfurization reaction is carried out in the presence of a base, which in one embodiment is the cation source, as described below.

In other embodiments the intermediate compound is contacted with formaldehyde or other aldehyde, which introduces alkylene bridging groups between polyolefin-substituted phenols in the presence of a base.

In general, sulfur coupling produces a more acidic compound which makes over-basing easier.

Formation of the salt may be performed by reaction of the sulfurized polyolefin-substituted compound or other sulfurized intermediate compound or alkylene bridged polyolefin-substituted compound with a basic metal compound which serves as a cation source, such as lime (calcium hydroxide/oxide) or magnesium oxide, or with a pnictogen base, in approximately equimolar amounts, with respect to the OH groups in the intermediate compound, optionally in the presence of a solvent.

Suitable basic metal compounds include hydroxides, oxides and alkoxides of the metal such as (1) an alkali metal salt derived from a metal base selected from an alkali hydroxide, alkali oxide or an alkali alkoxide, or (2) an alkaline earth metal salt derived from a metal base selected from an alkaline earth hydroxide, alkaline earth oxide or alkaline earth alkoxide. Representative examples of metal basic compounds with hydroxide functionality include lithium hydroxide, potassium hydroxide, sodium hydroxide, magnesium hydroxide, calcium hydroxide, barium hydroxide, aluminum hydroxide and the like. Representative examples of metal basic compounds with oxide functionality include lithium oxide, magnesium oxide, calcium oxide, barium oxide and the like. In one embodiment, the alkaline earth metal base is slaked lime (calcium hydroxide).

The pnictogen cation may be derived/derivable from a compound with a primary amine, a secondary amine, a tertiary amine, or mixtures thereof. Typically the amine salt may be derived from a secondary or a tertiary amine.

The amine that can be used to prepare a pnictogen may be any amine capable of salting with a protic acid. The amine may be an alkyl amine, typically a di- or tri-alkyl amine. The alkyl amine may have alkyl groups having 1 to 30, or 2 to 20, or 3 to 10 carbon atoms. Examples of a dialkyl amines include diethylamine, dipropylamine, dibutylamine, dipentylamine, dihexylamine, di-(2-ethylhexyl)amine, di-decylamine, di-dodecylamine, di-stearylamine, di-oleylamine, di-eicosylamine, or mixtures thereof. Examples of a trialkyl amine include triethylamine, tripropylamine, tributylamine, tripentylamine, trihexylamine, tri-(2-ethylhexyl)amine, tri-decylamine, tri-dodecylamine, tri-stearylamine, tri-oleylamine, tri-eicosylamine, and mixtures thereof.

The amine may also be a tertiary-aliphatic primary amine. The aliphatic group in this case may be an alkyl group containing 2 to 30, or 6 to 26, or 8 to 24 carbon atoms. Tertiary alkyl amines include monoamines such as tert-butylamine, tert-hexylamine, 1-methyl-1-amino-cyclohexane, tert-octylamine, tert-decylamine, tert-dodecylamine, tert-tetradecylamine, tert-hexadecylamine, tert-octadecylamine, tert-tetracosanylamine, and tert-octacosanylamine.

In one embodiment, the pnictogen base includes a phosphorus acid amine salt which includes an amine with C₁₁ to C₂₂ tertiary alkyl primary groups, or mixtures thereof.

In one embodiment the amine salt may be in the form of a quaternary ammonium salt. Examples of quaternary ammonium salts containing a hydroxyalkyl group, and methods for their synthesis, are disclosed in U.S. Pat. No. 3,962,104. In certain embodiments, the quaternary ammonium compound is derived from a monoamine by means of alkylation, i.e., from a tertiary amine having only a single amino group, that is, having no additional amine nitrogen atoms in any of the three hydrocarbyl groups or substituted hydrocarbyl groups attached to the tertiary amine nitrogen. In certain embodiments there are no additional amine nitrogen atoms in any of the hydrocarbyl groups or substituted hydrocarbyl groups attached to the central nitrogen in the quaternary ammonium ion. The tetraalkylammonium hydroxide may contain alkyl groups having 1 to 30, or 2 to 20, or 3 to 10 carbon atoms. The tetraalkylammonium hydroxide may include tetrapropylammonium hydroxide, tetrabutylammonium hydroxide, tetra-pentylammonium hydroxide, tetrahexylammonium hydroxide, tetra-2-ethylhexyl-ammonium hydroxide, tetradecylammonium hydroxide, or a mixture thereof.

The amine may be quaternized with a quaternizing agent, or mixture thereof.

The pnictogen base may include an aminoalkyl substituted heterocyclic compound, such as 1-(3-aminopropyl)imidazole, 4-(3-aminopropyl)morpholine, 1-(2-aminoethyl)piperidine, 3,3-diamino-N-methyldipropylamine, and 3,3-aminobis(N,N-dimethylpropylamine).

Other examples of quaternary ammonium salts and methods for preparing the same are described in U.S. Pat. Nos. 3,778,371, 4,171,959, 4,253,980, 4,326,973, 4,338,206, and 5,254,138.

When the amine salt is derived from an aromatic amine, the aromatic amine may form an ion such as a pyridinium ion, or an imidazolium ion. Certain quaternary phosphonium salts may be prepared by the reaction of phosphine with aldehydes and a halide e.g., tetrakis(hydroxymethyl)phosphonium halide (typically chloride).

A quaternary pnictogen halide compound may be a commercially available material, or it may be prepared by reaction of a tertiary amine with a hydrocarbyl halide, by known techniques. This reaction may be performed in a separate vessel or in the same vessel in which it is subsequently (or simultaneously) reacted with the oil-soluble acidic compound, which may be converted previously (or simultaneously) into its metal neutralized form.

Neutralization of the sulfurized intermediate compound may be carried out in a continuous or batch process by any method known to a person skilled in the art. In general, neutralization can be carried out by contacting the sulfurized or intermediate compound with a metal or pnictogen base under reactive conditions, e.g., in an inert-compatible liquid hydrocarbon diluent. If desired, the reaction can be conducted under an inert gas, such as nitrogen. The metal or pnictogen base may be added either in a single addition or in a plurality of additions at intermediate points during the reaction.

Neutralization may be conducted in a suitable solvent or diluent oil, such as toluene, xylene and commonly with a promoter such as an alcohol, e.g., a C₁ to C₁₆ alcohol, such as methanol, decyl alcohol, or 2-ethylhexanol; a diol, e.g., C₂ to C₄ alkylene glycols, such as ethylene glycol; and/or carboxylic acids. Suitable diluent oils include naphthenic oils and mixed oils, e.g., paraffinic. The quantity of solvent or diluent oil used may be such that the amount of solvent or oil in the final product constitutes from 15% to 65% by weight of the final product, such as from 25% to 50%.

The neutralization reaction may be conducted at temperatures above room temperature (20° C.). In general, neutralization can be carried out at a temperature of between 150-200° C. The neutralization reaction itself may take place for over 5 to 60 minutes up to 9 hours, for example, 7 hours.

In another embodiment, the salt of the polyolefin-substituted bridged hydroxyaromatic compound can be prepared in a one-pot method. In this method, the intermediate compound is combined with diluent oil and ethylene glycol and heated while stirring. A metal or pnictogen base, such as hydrated lime, is added to the heated reaction mixture, e.g., in several portions. Sulfur is added to the reaction mixture, and optionally additional metal or pnictogen base is added and the mixture stirred. The reaction mixture may be vacuum stripped to remove excess solvent.

In one embodiment, the exemplary polyolefin-substituted bridged hydroxyaromatic compound may be overbased. Overbasing can be carried out either during or after one of the sulfurization and/or neutralization steps. Alternatively, sulfurization, neutralization and overbasing can be carried out simultaneously. In general, the overbasing is carried out by reaction of the salt of the sulfur-coupled polyolefin-substituted aromatic polyol with an acidic overbasing compound, such as carbon dioxide or boric acid. In one embodiment, an overbasing process is by way of carbonation, i.e., a reaction with carbon dioxide. Such carbonation can be conveniently effected by addition of solvents such as aromatic solvents, alcohols or a polyols, typically an alkylene diol, e.g., ethylene glycol. Conveniently, the reaction is conducted by bubbling of gaseous carbon dioxide through the reaction mixture, optionally in the presence of sulfonic acid. Excess solvents and any water formed during the overbasing reaction can be conveniently removed by distillation either during or after the reaction.

In one embodiment, the overbasing reaction is carried out in a reactor by reacting the salt of the polyolefin-substituted bridged hydroxyaromatic compound with a source of an alkaline earth metal such as lime (i.e., an alkaline earth metal hydroxide) in the presence of carbon dioxide, and optionally in the presence of an aromatic solvent (e.g., xylene), and/or a hydrocarbyl alcohol, such as methanol. The reaction may be conducted by bubbling gaseous carbon dioxide through the reaction mixture. The carbon dioxide is introduced over a period of 1 hour to 3 hours, at a temperature ranging from 150-200° C. The degree of overbasing may be controlled by the quantity of the source of an alkaline earth metal, carbon dioxide and the reactants added to the reaction mixture and the reaction conditions used during the carbonation process.

In another embodiment, the overbasing reaction can be carried out at from 140-180° C. in the presence of a polyol, typically an alkylene diol, e.g., ethylene glycol, and/or alkanols, e.g., C₆ to C₁₆ alkanol(s), such as decyl alcohols or 2-ethyl hexanol. Excess solvent and any water formed during the overbasing reaction can be conveniently removed by distillation either during or after the reaction.

Methods for forming overbased detergents useful herein are described, for example, in U.S. Pat. Nos. 5,259,966, 6,015,778, 5,534,168, and 6,268,318, and U.S. Pub. No. 2013/0203639.

The resulting overbased salt of the polyolefin-substituted bridged hydroxyaromatic compound may contain some amount of unsulfurized hydroxy-substituted intermediate compound and/or its unsulfurized metal salt.

The composition containing the overbased salt of the polyolefin-substituted bridged hydroxyaromatic compound may be sparged, e.g., by bubbling gas, such as air or nitrogen, at a temperature ranging from 190−250° C. through the composition. The sparging results in removing substantially all of the unsulfurized hydroxy-substituted intermediate compound and salts thereof to provide a composition substantially free of the unsulfurized hydroxy-substituted intermediate compound and unsulfurized salts thereof. The term “substantially free” as used herein means less than 1.5 wt. %, or less than 1 wt. %, or less than 0.3 wt. % of these unsulfurized compounds, such as 0.1-0.3 wt. %, or less.

In one embodiment, the salt of the polyolefin-substituted bridged hydroxyaromatic compound does not contain any sulfonate functional groups.

In one embodiment, the salt of the polyolefin-substituted bridged hydroxyaromatic compound does not contain any phosphate functional groups.

In one embodiment, the salt of the polyolefin-substituted bridged hydroxyaromatic compound does not contain any borate functional groups.

In another embodiment, the salt of the polyolefin-substituted bridged hydroxyaromatic compound does contain a borate functional group.

The salts described above can be boronated by processes known to those skilled in the art. Boration can be accomplished either prior to, or after, the overbasing step. The boration can be accomplished by a number of boronating agents, such as boric acid, metaboric acid, orthoboric acid, alkyl borates, boron halides, polymers of boron, esters of boron and similar materials. When present, the boron content of the salt may be 0.1 wt. % to 5 wt. %, or 1 wt. % to 5 wt. %, or 2 wt. % to 4 wt. %.

The salt of the polyolefin-substituted bridged hydroxyaromatic compound, in one embodiment, may be formed from an anion composed of carbon, hydrogen, oxygen, boron and nitrogen; and a metallic cation.

In one embodiment, the salt of the polyolefin-substituted bridged hydroxyaromatic compound may comprise or consist of an anion composed of carbon, hydrogen, oxygen and optionally nitrogen; and a metallic cation, such as a calcium, magnesium or sodium cation.

Examples of suitable ethylenically unsaturated esters of boron include (meth)acrylates, fumarates and maleates which are derived from saturated alcohols, such as 2-ethylhexyl (meth)acrylate, heptyl (meth)acrylate, 2-tert-butylheptyl (meth)acrylate, octyl (meth)acrylate, 3-isopropylheptyl (meth)acrylate, nonyl (meth)acrylate, decyl (meth)acrylate, undecyl (meth)acrylate; and the corresponding fumarates and maleates. The expression “(meth)acrylates” encompasses methacrylates and acrylates and also mixtures of the two.

Lubricating Compositions

The exemplary polyolefin-substituted bridged hydroxyaromatic compound or salt thereof may be present in a lubricating composition at a concentration of at least 0.1 wt. % and may be up to 20 wt. %. For example, the concentration of the compound may be at least 0.25 wt. %, or at least 0.5 wt. %, or at least 1 wt. %, or at least 5 wt. %, or at least 10 wt. %, or at least 15 wt. % of the lubricating composition. The compound may also be present in a concentrate, alone or with other additives and with a lesser amount of oil. In a concentrate, the amount of the compound may be at least 2, or at least 3 times the concentration in the lubricating composition.

In addition to the polyolefin-substituted bridged hydroxyaromatic compound or metal salt thereof, the exemplary lubricating composition includes an oil of lubricating viscosity and optionally one or more additional performance additives suited to providing the performance properties of a fully formulated lubricating composition, e.g., a marine diesel cylinder lubricant. Examples of these additional performance additives include (overbased) detergents, viscosity modifiers, friction modifiers, antioxidants, dispersants, antiwear/antiscuffing agents, metal deactivators, extreme pressure agents, foam inhibitors, demulsifiers, pour point depressants, corrosion inhibitors, seal swelling agents, and the like, which may be used singly or in combination.

Oil of Lubricating Viscosity

The lubricating composition may include the oil of lubricating viscosity as a minor or major component thereof, such as at least 5 wt. %, or at least 10 wt. %, or at least 20 wt. %, or at least 30 wt. %, or at least 40 wt. %, or at least 60 wt. %, or at least 80 wt. % of the lubricating composition.

Suitable oils include natural and synthetic oils, oil derived from hydrocracking, hydrogenation, and hydrofinishing, unrefined, refined, re-refined oils or mixtures thereof. Unrefined, refined and re-refined oils, and natural and synthetic oils are described, for example, in WO2008/147704 and US Pub. No. 2010/197536. Synthetic oils may also be produced by Fischer-Tropsch reactions and typically may be hydroisomerized Fischer-Tropsch hydrocarbons or waxes. Oils may be prepared by a Fischer-Tropsch gas-to-liquid synthetic procedure as well as other gas-to-liquid procedures.

Oils of lubricating viscosity may also be defined as specified in April 2008 version of “Appendix E—API Base Oil Interchangeability Guidelines for Passenger Car Motor Oils and Diesel Engine Oils”, section 1.3 Sub-heading 1.3. “Base Stock Categories”. The API Guidelines are also summarized in U.S. Pat. No. 7,285,516. The five base oil groups are as follows: Group I (sulfur content>0.03 wt. %, and/or <90 wt. % saturates, viscosity index 80-120); Group II (sulfur content≤0.03 wt. %, and ≥90 wt. % saturates, viscosity index 80-120); Group III (sulfur content≤0.03 wt. %, and ≥90 wt. % saturates, viscosity index≥120); Group IV (all polyalphaolefins (PAOs)); and Group V (all others not included in Groups I, II, III, or IV). The exemplary oil of lubricating viscosity includes an API Group I, Group II, Group III, Group IV, Group V oil, or mixtures thereof. In some embodiments, the oil of lubricating viscosity is an API Group I, Group II, Group III, or Group IV oil, or mixtures thereof. In some embodiments, the oil of lubricating viscosity is an API Group I, Group II, or Group III oil, or mixture thereof. In one embodiment the oil of lubricating viscosity may be an API Group II, Group III mineral oil, a Group IV synthetic oil, or mixture thereof. In some embodiments, at least 5 wt. %, or at least 10 wt. %, or at least 20 wt. %, or at least 40 wt. % of the lubricating composition is a polyalphaolefin (Group IV).

Engine Lubricating Compositions

For lubricating compositions useful in engines, the oil of lubricating viscosity may have a kinematic viscosity of up to 30 mm²/s or up to 25 mm²/s (cSt) at 100° C. and can be at least 12 mm²/s at 100° C., and in other embodiments at least 15 mm²/s. As used herein, kinematic viscosity is determined at 100° C. by ASTM D445-14, “Standard Test Method for Kinematic Viscosity of Transparent and Opaque Liquids (and Calculation of Dynamic Viscosity),” ASTM International, West Conshohocken, Pa., 2003, DOI: 10.1520/D0445-14 and may be referred to as KV_100.

The viscosity grade of cylinder oils suited to use in 2-stroke marine diesel engines may be from SAE-40 to SAE-60, which corresponds to a KV_100 of 12.5 to 26 mm²/s. SAE-50 grade oils, for example, have a KV_100 of 16.3-21.9 mm²/s. Cylinder oils for 2-stroke marine diesel engines may be formulated to achieve a KV_100 of 19 to 21.5 mm²/s. This viscosity can be obtained by a mixture of additives and base oils, for example containing mineral bases of Group I such as Neutral Solvent (for example 500 NS or 600 NS) and Bright Stock bases. Any other combination of mineral or synthetic bases or bases of vegetable origin having, in mixture with the additives, a viscosity compatible with the grade SAE 50 can be used.

As an example, an oil formulation suited to use as a cylinder lubricant for low-speed 2-stroke marine diesel engines contains 18 to 25 wt. % of a Group I base oil of a BSS type (distillation residue, with a KV_100 of 28-32 mm²/s, with a density at 15° C. of 895-915 kg/m³), and 50 to 60 wt. % of a Group I base oil of a SN 600 type (distillate, with a density at 15° C. of 880-900 kg/m³, with a KV_100 of about 12 mm²/s).

In certain embodiments, the lubricating composition may contain synthetic ester base fluids. Synthetic esters may have a kinematic viscosity measured at 100° C. of 2.5 mm²/s to 30 mm²/s. In one embodiment, the lubricating composition comprises less than 50 wt. % of a synthetic ester base fluid with a KV_100 of at least 5.5 mm²/s, or at least 6 mm²/s, or at least 8 mm²/s.

Exemplary synthetic oils include poly-alpha olefins, polyesters, polyacrylates, and poly-methacrylates, and co-polymers thereof. Example synthetic esters include esters of a dicarboxylic acid (e.g., selected from phthalic acid, succinic acid, alkyl succinic acids, alkenyl succinic acids, maleic acid, azelaic acid, suberic acid, sebacic acid, fumaric acid, adipic acid, linoleic acid dimer, malonic acid, alkyl malonic acids, and alkenyl malonic acids) with an alcohol (e.g., selected from butyl alcohol, hexyl alcohol, dodecyl alcohol, 2-ethylhexyl alcohol, ethylene glycol, diethylene glycol monoether, and propylene glycol). Specific examples of these esters include dibutyl adipate, di(2-ethylhexyl) sebacate, di-n-hexyl fumarate, dioctyl sebacate, diisooctyl azelate, diisodecyl azelate, dioctyl phthalate, didecyl phthalate, dieicosyl sebacate, the 2-ethylhexyl diester of linoleic acid dimer, and the complex ester formed by reacting one mole of sebacic acid with two moles of tetraethylene glycol and two moles of 2-ethylhexanoic acid.

Esters useful as synthetic oils also include those made from C₅ to C₁₂ monocarboxylic acids and polyols and from polyol ethers such as neopentyl glycol, trimethylolpropane, pentaerythritol, dipentaerythritol, and tripentaerythritol. Esters can also be monoesters, such as are available under the trade name Priolube 1976™ (C₁₈-alkyl-COO—C₂₀ alkyl).

Synthetic ester base oils may be present in the lubricating composition of the invention in an amount less than 50 wt. % of the composition, or less than 40 weight %, or less than 35 weight %, or less than 28 weight %, or less than 21 weight %, or less than 17 weight %, or less than 10 weight %, or less than 5 weight % of the composition. In one embodiment, the lubricating composition of the invention is free of, or substantially free of, a synthetic ester base fluid having a KV_100 of at least 5.5 mm²/s.

Example natural oils include animal and vegetable oils, such as long chain fatty acid esters. Examples include linseed oil, sunflower oil, sesame seed oil, beef tallow oil, lard oil, palm oil, castor oil, cottonseed oil, corn oil, peanut oil, soybean oil, olive oil, whale oil, menhaden oil, sardine oil, coconut oil, palm kernel oil, babassu oil, rape oil, and soya oil.

The amount of the oil of lubricating viscosity present is typically the balance remaining after subtracting from 100 weight % the sum of the amount of the exemplary amino-carboxylate compound and the other performance additives.

Engine Lubricating Compositions—Other Additives

Engine lubricating compositions in accordance with the present invention may also contain other additives that provide particular performance benefits to the engine lubricant. These additional additives may include detergents, antioxidants, dispersants, anti-wear agents, oil-soluble titanium compounds, extreme pressure agents, foam inhibitors, viscosity modifiers, corrosion inhibitors, metal deactivators, pour point depressants, friction modifiers, demulsifiers, and seal swell agents. These additional components are described in more detail below.

The lubricating composition optionally further includes at least one detergent, other than the exemplary compound. Exemplary detergents useful herein include overbased metal-containing detergents. The metal of the metal-containing detergent may be zinc, sodium, calcium, barium, or magnesium. The overbased metal-containing detergent may be chosen from sulfonates, non-sulfur containing phenates, sulfur containing phenates, salixarates, salicylates, and mixtures thereof, or borated equivalents thereof. The overbased detergent may be borated with a borating agent such as boric acid.

The overbased metal-containing detergent may also include “hybrid” detergents formed with mixed surfactant systems including phenate and/or sulfonate components, e.g., phenate/salicylates, sulfonate/phenates, sulfonate/salicylates, sulfonates/phenates/salicylates, as described, for example, in U.S. Pat. Nos. 6,429,178; 6,429,179; 6,153,565; and 6,281,179. Where a hybrid sulfonate/phenate detergent is employed, the hybrid detergent can be considered equivalent to amounts of distinct phenate and sulfonate detergents introducing like amounts of phenate and sulfonate soaps, respectively.

Example overbased metal-containing detergents include zinc, sodium, calcium and magnesium salts of sulfonates, phenates (including sulfur-containing and non-sulfur containing phenates), salixarates and salicylates. Such overbased sulfonates, salixarates, phenates and salicylates may have a total base number of 120 to 700, or 250 to 600, or 300 to 500 (on an oil free basis).

The overbased sulfonate detergent may have a metal ratio of 12 to less than 20, or 12 to 18, or 20 to 30, or 22 to 25.

Typically, an overbased metal-containing detergent may be a zinc, sodium, calcium or magnesium salt of a sulfonate, a phenate, sulfur containing phenate, salixarate or salicylate. Overbased sulfonates, salixarates, phenates and salicylates typically have a total base number of 120 to 700 TBN. Overbased sulfonates typically have a total base number of 120 to 700, or 250 to 600, or 300 to 500 (on an oil free basis).

The overbased sulfonate detergent may have a metal ratio of 12 to less than 20, or 12 to 18, or 20 to 30, or 22 to 25.

Example sulfonate detergents include linear and branched alkylbenzene sulfonate detergents, and mixtures thereof, which may have a metal ratio of at least 8, as described, for example, in U.S. Pub. No. 2005065045. Linear alkyl benzenes may have the benzene ring attached anywhere on the linear chain, usually at the 2, 3, or 4 position, or be mixtures thereof. Linear alkylbenzene sulfonate detergents may be particularly useful for assisting in improving fuel economy.

In one embodiment, the alkylbenzene sulfonate detergent may be a branched alkylbenzene sulfonate, a linear alkylbenzene sulfonate, or mixtures thereof.

In one embodiment, the lubricating composition may be free of linear alkylbenzene sulfonate detergent. The sulfonate detergent may be a metal salt of one or more oil-soluble alkyl toluene sulfonate compounds as disclosed in U.S. Pub. No. 20080119378.

The lubricating composition may include at least 0.01 wt. % or at least 0.1 wt. % of the detergent other than the exemplary compound, and in some embodiments, up to 2 wt. %, or up to 1 wt. % detergent.

The lubricating composition optionally further includes at least one antioxidant. Exemplary antioxidants useful herein include phenolic and aminic antioxidants, such as diarylamines, alkylated diarylamines, hindered phenols, and mixtures thereof. The diarylamine or alkylated diarylamine may be a phenyl-α-naphthylamine (PANA), an alkylated diphenylamine, an alkylated phenylnapthylamine, or mixture thereof. Example alkylated diphenylamines include dinonyl diphenylamine, nonyl diphenylamine, octyl diphenylamine, dioctyl diphenylamine, didecyl diphenylamine, decyl diphenylamine, and mixtures thereof. Example alkylated diarylamines include octyl, dioctyl, nonyl, dinonyl, decyl and didecyl phenylnapthylamines. Hindered phenol antioxidants often contain a secondary butyl and/or a tertiary butyl group as a steric hindering group. The phenol group may be further substituted with a hydrocarbyl group (e.g., a linear or branched alkyl) and/or a bridging group linking to a second aromatic group. Examples of suitable hindered phenol antioxidants include 2,6-di-tert-butylphenol, 4-methyl-2,6-di-tert-butylphenol, 4-ethyl-2,6-di-tert-butylphenol, 4-propyl-2,6-di-tert-butylphenol, 4-butyl-2,6-di-tert-butylphenol, and 4-dodecyl-2,6-di-tert-butylphenol. In one embodiment, the hindered phenol antioxidant may be an ester, such as those described in U.S. Pat. No. 6,559,105. One such hindered phenol ester is sold as Irganox™ L-135, obtainable from Ciba.

When present, the lubricating composition may include at least 0.1 wt. % or at least 0.5 wt. %, or at least 1 wt. % antioxidant, and in some embodiments, up to 3 wt. %, or up to 2.75 wt. %, or up to 2.5 wt. % antioxidant.

The lubricating composition optionally further includes at least one dispersant, other than the exemplary compound. Exemplary dispersants include succinimide dispersants, Mannich dispersants, succinamide dispersants, and polyolefin succinic acid esters, amides, and ester-amides, and mixtures thereof. The succinimide dispersant, where present, may be as described above for the succinimides described as useful for cation M.

The succinimide dispersant may be derived from an aliphatic polyamine, or mixtures thereof. The aliphatic polyamine may be an ethylenepolyamine, a propylenepolyamine, a butylenepolyamine, or a mixture thereof. In one embodiment the aliphatic polyamine may be an ethylenepolyamine. In one embodiment the aliphatic polyamine may be chosen from ethylenediamine, diethylenetriamine, triethylenetetramine, tetraethylenepentamine, pentaethylenehexamine, polyamine still bottoms, and mixtures thereof.

In one embodiment, the dispersant may be a polyolefin succinic acid ester, amide, or ester-amide. A polyolefin succinic acid ester-amide may be a polyisobutylene succinic acid reacted with an alcohol (such as pentaerythritol) and a polyamine as described above. Example polyolefin succinic acid esters include polyisobutylene succinic acid esters of pentaerythritol and mixture thereof.

The dispersant may be an N-substituted long chain alkenyl succinimide. An example of an N-substituted long chain alkenyl succinimide is polyisobutylene succinimide. Typically the polyisobutylene from which polyisobutylene succinic anhydride is derived has a number average molecular weight of 350 to 5000, or 550 to 3000 or 750 to 2500. Succinimide dispersants and their preparation are disclosed, for example, in U.S. Pat. Nos. 3,172,892, 3,219,666, 3,316,177, 3,340,281, 3,351,552, 3,381,022, 3,433,744, 3,444,170, 3,467,668, 3,501,405, 3,542,680, 3,576,743, 3,632,511, 4,234,435, Re 26,433, and 6,165,235, and 7,238,650 and EP Patent Application 0 355 895 A.

The succinimide dispersant may comprise a polyisobutylene succinimide, wherein the polyisobutylene from which polyisobutylene succinimide is derived has a number average molecular weight of 350 to 5000, or 750 to 2500.

The exemplary dispersants may also be post-treated by conventional methods by a reaction with any of a variety of agents. Among these are boron compounds (such as boric acid), urea, thiourea, dimercaptothiadiazoles, carbon disulfide, aldehydes, ketones, carboxylic acids, such as terephthalic acid, hydrocarbon-substituted succinic anhydrides, maleic anhydride, nitriles, epoxides, and phosphorus compounds. In one embodiment the post-treated dispersant is borated. In one embodiment the post-treated dispersant is reacted with dimercaptothiadiazoles. In one embodiment the post-treated dispersant is reacted with phosphoric or phosphorous acid. In one embodiment the post-treated dispersant is reacted with terephthalic acid and boric acid (as described in U.S. Pub. No. 2009/0054278.

When present, the lubricating composition may include at least 0.01 wt. %, or at least 0.1 wt. %, or at least 0.5 wt. %, or at least 1 wt. % of other dispersant(s), and in some embodiments, up to 20 wt. %, or up to 15 wt. %, or up to 10 wt. %, or up to 6 wt. % or up to 3 wt. % dispersant.

The lubricating composition optionally further includes at least one antiwear agent. Examples of suitable antiwear agents suitable for use herein include titanium compounds, tartrates, tartrimides, oil soluble amine salts of phosphorus compounds, sulfurized olefins, metal dihydrocarbyldithiophosphates (such as zinc dialkyldithiophosphates), phosphites (such as dibutyl phosphite), phosphonates, thiocarbamate-containing compounds, such as thiocarbamate esters, thiocarbamate amides, thiocarbamic ethers, alkylene-coupled thiocarbamates, and bis(S-alkyldithiocarbamyl) disulfides. The antiwear agent may in one embodiment include a tartrate, or tartrimide as described in U.S. Pub. Nos. 2006/0079413; 2006/0183647; and 2010/0081592. The tartrate or tartrimide may contain alkyl-ester groups, where the sum of carbon atoms on the alkyl groups is at least 8. The antiwear agent may, in one embodiment, include a citrate as is disclosed in US Pub. No. 20050198894.

The lubricating composition may in one embodiment further include a phosphorus-containing antiwear agent. Example phosphorus-containing antiwear agents include zinc dialkyldithiophosphates, phosphites, phosphates, phosphonates, and ammonium phosphate salts, and mixtures thereof.

When present, the lubricating composition may include at least 0.01 wt. %, or at least 0.1 wt. %, or at least 0.5 wt. % antiwear agent, and in some embodiments, up to 3 wt. %, or up to 1.5 wt. %, or up to 0.9 wt. antiwear agent.

The lubricating composition may include one or more oil-soluble titanium compounds, which may function as antiwear agents, friction modifiers, antioxidants, deposit control additives, or more than one of these functions. Example oil-soluble titanium compounds are disclosed in U.S. Pat. No. 7,727,943 and U.S. Pub. No. 2006/0014651. Example oil soluble titanium compounds include titanium (IV) alkoxides, such as titanium (IV) isopropoxide and titanium (IV) 2 ethylhexoxide. Such alkoxides may be formed from a monohydric alcohol, a vicinal 1,2-diol, a polyol, or mixture thereof. The monohydric alkoxides may have 2 to 16, or 3 to 10 carbon atoms. In one embodiment, the titanium compound comprises the alkoxide of a vicinal 1,2-diol or polyol. 1,2-vicinal diols include fatty acid mono-esters of glycerol, where the fatty acid may be, for example, oleic acid. Other example oil soluble titanium compounds include titanium carboxylates, such as titanium neodecanoate.

When present in the lubricating composition, the amount of oil-soluble titanium compounds is included as part of the antiwear agent.

The lubricating composition may include an extreme pressure agent. Example extreme pressure agents that are soluble in the oil include sulfur- and chlorosulfur-containing EP agents, dimercaptothiadiazole or CS₂ derivatives of dispersants (typically succinimide dispersants), derivative of chlorinated hydrocarbon EP agents and phosphorus EP agents. Examples of such EP agents include chlorinated wax; sulfurized olefins (such as sulfurized isobutylene), hydrocarbyl-substituted 2,5-dimercapto-1,3,4-thiadiazoles and oligomers thereof, organic sulfides and polysulfides, such as dibenzyldisulfide, bis-(chlorobenzyl) disulfide, dibutyl tetrasulfide, sulfurized methyl ester of oleic acid, sulfurized alkylphenol, sulfurized dipentene, sulfurized terpene, and sulfurized Diels-Alder adducts; phosphosulfurized hydrocarbons such as the reaction product of phosphorus sulfide with turpentine or methyl oleate; phosphorus esters, such as dihydrocarbon and trihydrocarbon phosphites, e.g., dibutyl phosphite, diheptyl phosphite, dicyclohexyl phosphite, pentylphenyl phosphite; dipentylphenyl phosphite, tridecyl phosphite, distearyl phosphite and polypropylene substituted phenol phosphite; metal thiocarbamates, such as zinc dioctyldithiocarbamate and barium heptylphenol diacid; amine salts of alkyl and dialkylphosphoric acids or derivatives including, for example, the amine salt of a reaction product of a dialkyldithiophosphoric acid with propylene oxide and subsequently followed by a further reaction with P₂O₅; and mixtures thereof. Some useful extreme pressure agents are described in U.S. Pat. No. 3,197,405.

When present, the lubricating composition may include at least 0.01 wt. %, or at least 0.1 wt. %, or at least 0.5 wt. % extreme pressure agent, and in some embodiments, up to 3 wt. %, or up to 1.5 wt. %, or up to 0.9 wt. % of the extreme pressure agent.

The lubricating composition may include a foam inhibitor. Foam inhibitors that may be useful in the lubricant composition include polysiloxanes; copolymers of ethyl acrylate and 2-ethylhexylacrylate and optionally vinyl acetate; demulsifiers including fluorinated polysiloxanes, trialkyl phosphates, polyethylene glycols, polyethylene oxides, polypropylene oxides and (ethylene oxide-propylene oxide) polymers.

The lubricating composition may include a viscosity modifier. Viscosity modifiers (also sometimes referred to as viscosity index improvers or viscosity improvers) useful in the lubricant composition are usually polymers, including polyisobutenes, polymethacrylates (PMA) and polymethacrylic acid esters, diene polymers, polyalkylstyrenes, esterified styrene-maleic anhydride copolymers, hydrogenated alkenylarene-conjugated diene copolymers and polyolefins also referred to as olefin copolymer or OCP. PMA's are prepared from mixtures of methacrylate monomers having different alkyl groups. The alkyl groups may be either straight chain or branched chain groups containing from 1 to 18 carbon atoms. Most PMA's are viscosity modifiers as well as pour point depressants. In one embodiment, the viscosity modifier is a polyolefin comprising ethylene and one or more higher olefin, such as propylene.

When present, the lubricating composition may include at least 0.01 wt. %, or at least 0.1 wt. %, or at least 0.3 wt. %, or at least 0.5 wt. % polymeric viscosity modifiers, and in some embodiments, up to 10 wt. %, or up to 5 wt. %, or up to 2.5 wt. % polymeric viscosity modifiers.

The lubricating composition may include a corrosion inhibitor. Corrosion inhibitors/metal deactivators that may be useful in the exemplary lubricating composition include fatty amines, octylamine octanoate, condensation products of dodecenyl succinic acid or anhydride, and a fatty acid such as oleic acid with a polyamine, derivatives of benzotriazoles (e.g., tolyltriazole), 1,2,4-triazoles, benzimidazoles, 2-alkyldithiobenzimidazoles and 2-alkyldithiobenzothiazoles.

The lubricating composition may include a pour point depressant. Pour point depressants that may be useful in the exemplary lubricating composition include polyalphaolefins, esters of maleic anhydride-styrene copolymers, polymethacrylates, polyacrylates, and polyacrylamides.

The lubricating composition may include a friction modifier. Friction modifiers that may be useful in the exemplary lubricating composition include fatty acid derivatives such as amines, esters, epoxides, fatty imidazolines, condensation products of carboxylic acids and polyalkylene-polyamines and amine salts of alkylphosphoric acids. The friction modifier may be an ash-free friction modifier. Such friction modifiers are those which typically not produce any sulfated ash when subjected to the conditions of ASTM D 874. An additive is referred to as “non-metal containing” if it does not contribute metal content to the lubricant composition. As used herein the term “fatty alkyl” or “fatty” in relation to friction modifiers means a carbon chain having 8 to 30 carbon atoms, typically a straight carbon chain.

In one embodiment, the ash-free friction modifier may be represented by the formula:

where, D and D′ are independently selected from —O—, >NH, >NR²³, an imide group formed by taking together both D and D′ groups and forming a R²¹—N< group between two >C═O groups; E is selected from —R²⁴—O—R²⁵—, >CH₂, >CHR²⁶, >CR²⁶R²⁷, >C(OH)(CO₂R²²), >C(CO₂R²²)₂, and >CHOR²⁸; where R²⁴ and R²⁵ are independently selected from >CH₂, >CHR²⁶, >CR²⁶R²⁷, >C(OH)(CO₂R²²), and >CHOR²⁸; q is 0 to 10, with the proviso that when q=1, E is not >CH₂, and when n=2, both Es are not >CH₂; p is 0 or 1; R²¹ is independently hydrogen or a hydrocarbyl group, typically containing 1 to 150 carbon atoms, with the proviso that when R²¹ is hydrogen, p is 0, and q is more than or equal to 1; R²² is a hydrocarbyl group, typically containing 1 to 150 carbon atoms; R²³, R²⁴, R²⁵, R²⁶ and R²⁷ are independently hydrocarbyl groups; and R²⁸ is hydrogen or a hydrocarbyl group, typically containing 1 to 150 carbon atoms, or 4 to 32 carbon atoms, or 8 to 24 carbon atoms. In certain embodiments, the hydrocarbyl groups R²³, R²⁴, and R²⁵, may be linear or predominantly linear alkyl groups.

In certain embodiments, the ash-free friction modifier is a fatty ester, amide, or imide of various hydroxy-carboxylic acids, such as tartaric acid, malic acid lactic acid, glycolic acid, and mandelic acid. Examples of suitable materials include tartaric acid di(2-ethylhexyl) ester (i.e., di(2-ethylhexyl)tartrate), di(C₈-C₁₀)tartrate, di(C₁₂₋₁₅)tartrate, di-oleyltartrate, oleyltartrimide, and oleyl maleimide.

In certain embodiments, the ash-free friction modifier may be chosen from long chain fatty acid derivatives of amines, fatty esters, or fatty epoxides; fatty imidazolines such as condensation products of carboxylic acids and polyalkylene-polyamines; amine salts of alkylphosphoric acids; fatty alkyl tartrates; fatty alkyl tartrimides; fatty alkyl tartramides; fatty phosphonates; fatty phosphites; borated phospholipids, borated fatty epoxides; glycerol esters; borated glycerol esters; fatty amines; alkoxylated fatty amines; borated alkoxylated fatty amines; hydroxyl and polyhydroxy fatty amines including tertiary hydroxy fatty amines; hydroxy alkyl amides; metal salts of fatty acids; metal salts of alkyl salicylates; fatty oxazolines; fatty ethoxylated alcohols; condensation products of carboxylic acids and polyalkylene polyamines; or reaction products from fatty carboxylic acids with guanidine, aminoguanidine, urea, or thiourea and salts thereof.

Friction modifiers may also encompass materials such as sulfurized fatty compounds and olefins, sunflower oil or soybean oil monoester of a polyol and an aliphatic carboxylic acid.

In another embodiment the friction modifier may be a long chain fatty acid ester. In another embodiment the long chain fatty acid ester may be a monoester and in another embodiment the long chain fatty acid ester may be a triglyceride.

The amount of the ash-free friction modifier in a lubricant may be 0.1 to 3 percent by weight (or 0.12 to 1.2 or 0.15 to 0.8 percent by weight). The material may also be present in a concentrate, alone or with other additives and with a lesser amount of oil. In a concentrate, the amount of material may be two to ten times the above concentration amounts.

Molybdenum compounds are also known as friction modifiers. The exemplary molybdenum compound does not contain dithiocarbamate moieties or ligands.

Nitrogen-containing molybdenum materials include molybdenum-amine compounds, as described in U.S. Pat. No. 6,329,327, and organomolybdenum compounds made from the reaction of a molybdenum source, fatty oil, and a diamine as described in U.S. Pat. No. 6,914,037. Other molybdenum compounds are disclosed in U.S. Pub. No. 20080280795. Molybdenum amine compounds may be obtained by reacting a compound containing a hexavalent molybdenum atom with a primary, secondary or tertiary amine represented by the formula NR²⁹R³⁰R³¹, where each of R²⁹, R³⁰ and R³¹ is independently hydrogen or a hydrocarbyl group of 1 to 32 carbon atoms and wherein at least one of R²⁹, R³⁰ and R³¹ is a hydrocarbyl group of 4 or more carbon atoms or represented by the formula:

where R³² represents a chain hydrocarbyl group having 10 or more carbon atoms, s is 0 or 1, R³³ and/or R³⁴ represents a hydrogen atom, a hydrocarbyl group, an alkanol group or an alkyl amino group having 2 to 4 carbon atoms, and when s=0, both R³³ and R³⁴ are not hydrogen atoms or hydrocarbon groups.

Specific examples of suitable amines include monoalkyl (or alkenyl) amines such as tetradecylamine, stearylamine, oleylamine, beef tallow alkylamine, hardened beef tallow alkylamine, and soybean oil alkylamine; dialkyl(or alkenyl)amines such as N-tetradecylmethylamine, N-pentadecylmethylamine, N-hexadecylmethylamine, N-stearylmethylamine, N-oleylmethylamine, N-dococylmethylamine, N-beef tallow alkyl methylamine, N-hardened beef tallow alkyl methylamine, N-soybean oil alkyl methylamine, ditetradecylamine, dipentadecylamine, dihexadecylamine, distearylamine, dioleylamine, didococylamine, bis(2-hexyldecyl)amine, bis(2-octyldodecyl)amine, bis(2-decyltetradecyl)amine, beef tallow dialkylamine, hardened beef tallow dialkylamine, and soybean oil dialkylamine; and trialk(en)ylamines such as tetradecyldimethylamine, hexadecyldimethylamine, octadecyldimethylamine, beef tallow alkyldimethylamine, hardened beef tallow alkyldimethylamine, soybean oil alkyldimethylamine, dioleylmethylamine, tritetradecylamine, tristearylamine, and trioleylamine. Suitable secondary amines have two alkyl (or alkenyl) groups with 14 to 18 carbon atoms.

Examples of the compound containing the hexavalent molybdenum atom include molybdenum trioxides or hydrates thereof (MoO₃.nH₂O), molybdenum acid (H₂MoO₄), alkali metal molybdates (Q₂MoO₄) wherein Q represents an alkali metal such as sodium and potassium, ammonium molybdates {(NH₄)₂MoO₄ or heptamolybdate (NH₄)₆[Mo₇O₂₄].4H₂O}, MoOCl₄, MoO₂Cl₂, MoO₂Br₂, Mo₂O₃Cl₆ and the like. Molybdenum trioxides or hydrates thereof, molybdenum acid, alkali metal molybdates and ammonium molybdates are often suitable because of their availability. In one embodiment, the lubricating composition comprises molybdenum amine compound.

Other organomolybdenum compounds of the invention may be the reaction products of fatty oils, mono-alkylated alkylene diamines and a molybdenum source. Materials of this sort are generally made in two steps, a first step involving the preparation of an aminoamide/glyceride mixture at high temperature, and a second step involving incorporation of the molybdenum.

Examples of fatty oils that may be used include cottonseed oil, groundnut oil, coconut oil, linseed oil, palm kernel oil, olive oil, corn oil, palm oil, castor oil, rapeseed oil (low or high erucic acids), soyabean oil, sunflower oil, herring oil, sardine oil, and tallow. These fatty oils are generally known as glyceryl esters of fatty acids, triacylglycerols or triglycerides.

Examples of some mono-alkylated alkylene diamines that may be used include methylaminopropylamine, methylaminoethylamine, butylaminopropylamine, butylamino-ethylamine, octylaminopropylamine, octylaminoethylamine, dodecylaaminopropylaamine, dodecylaminoethylamine, hexadecylaminopropylamine, hexadecylaminoethylamine, octadecyl-aminopropylamine, octadecylaminoethylamine, isopropyloxypropyl-1,3-diaminopropane, and octyloxypropyl-1,3-diaminopropane. Mono-alkylated alkylene diamines derived from fatty acids may also be used. Examples include N-coco alkyl-1,3-propanediamine (Duomeen®C), N-tall oil alkyl-1,3-propanediamine (Duomeen®T) and N-oleyl-1,3-propanediamine (Duomeen®O), all commercially available from Akzo Nobel.

Sources of molybdenum for incorporation into the fatty oil/diamine complex are generally oxygen-containing molybdenum compounds include, similar to those above, ammonium molybdates, sodium molybdate, molybdenum oxides and mixtures thereof. One suitable molybdenum source comprises molybdenum trioxide (MoO₃).

Nitrogen-containing molybdenum compounds which are commercially available include, for example, Sakuralube® 710 available from Adeka which is a molybdenum amine compound, and Molyvan® 855, available from R.T. Vanderbilt.

The nitrogen-containing molybdenum compound may be present in the lubricant composition at 0.005 to 2 wt. % of the composition, or 0.01 to 1.3 wt. %, or 0.02 to 1.0 wt. % of the composition. The molybdenum compound may provide the lubricant composition with 0 to 1000 ppm, or 5 to 1000 ppm, or 10 to 750 ppm 5 ppm to 300 ppm, or 20 ppm to 250 ppm of molybdenum.

Demulsifiers useful herein include trialkyl phosphates, and various polymers and copolymers of ethylene glycol, ethylene oxide, propylene oxide, and mixtures thereof.

Seal swell agents useful herein include sulfolene derivatives such as Exxon Necton-37™ (FN 1380) and Exxon Mineral Seal Oil™ (FN 3200).

Example Engine Lubricating Compositions

An engine lubricant in different embodiments may have a composition as illustrated in Table 1. All additives are expressed on an oil-free basis.

TABLE 1 Example Engine Lubricating Compositions Embodiments (wt. %) Additive A B   C polyolefin-substituted bridged 0.1 to 20    0.5 to 10    1 to 5 hydroxyaromatic compound or salt thereof Overbased Sulfonate Detergent 0 to 9   0.3 to 8     1 to 5 Phenol-based detergent 0 to 10  0.5 to 7  0.75 to 5 (Borated) Dispersant 0 to 12  0.5 to 8     1 to 5 Antioxidant 0 to 13  0.1 to 10  0.5 to 5 Antiwear Agent 0 to 15  0.1 to 10  0.3 to 5 Corrosion Inhibitor 0 to 2   0.1 to 1     0.2 to 0.5 Friction Modifier 0 to 6  0.05 to 4   0.1 to 2 Viscosity Modifier 0 to 10  0.5 to 8     1 to 6 Other Performance Additives 0 to 10    0 to 8     0 to 6 Oil of Lubricating Viscosity Balance to 100%

Use of the Lubricating Composition

The end use of the engine lubricating composition described herein includes use as a cylinder lubricant for an internal combustion engine, such as a 2-stroke marine diesel engine, but may also find use as an engine oil for a two or 4-stroke engine in a passenger car, heavy, medium and light duty diesel vehicles, small engines such as motorcycle and 2-stroke oil engines, as a driveline lubricant, including gear and automatic transmission oils, and for other industrial oils, such as hydraulic lubricants.

An exemplary method of lubricating a mechanical device, such as a cylinder of an internal combustion engine, includes supplying the exemplary lubricating composition to the device.

Generally, the lubricating composition is added to the lubricating system of an internal combustion engine, which then delivers the lubricating composition to the cylinder of the engine, during its operation, where it may be combusted with the fuel.

The internal combustion engine may be a diesel-fueled engine, such as a 2-stroke marine diesel engine, or a gasoline fueled engine, a natural gas fueled engine, a mixed gasoline/alcohol fueled engine, or a biodiesel fueled engine. The internal combustion engine may be a 2-stroke or 4-stroke engine.

The lubricating composition may be suitable for use as a cylinder lubricant irrespective of the sulfur, phosphorus or sulfated ash (ASTM D-874) content of the fuel. The sulfur content of the lubricating composition, which is particularly suited to use as an engine oil lubricant, may be 1 wt. % or less, or 0.8 wt. % or less, or 0.5 wt. % or less, or 0.3 wt. % or less. In one embodiment, the sulfur content may be in the range of 0.001 wt. % to 0.5 wt. %, or 0.01 wt. % to 0.3 wt. %. The phosphorus content may be 0.2 wt. % or less, or 0.12 wt. % or less, or 0.1 wt. % or less, or 0.085 wt. % or less, or 0.08 wt. % or less, or even 0.06 wt. % or less, 0.055 wt. % or less, or 0.05 wt. % or less. In one embodiment, the phosphorus content may be 100 ppm to 1000 ppm, or 200 ppm to 600 ppm. The total sulfated ash content may be 2 wt. % or less, or 1.5 wt. % or less, or 1.1 wt. % or less, or 1 wt. % or less, or 0.8 wt. % or less, or 0.5 wt. % or less, or 0.4 wt. % or less. In one embodiment, the sulfated ash content may be 0.05 wt. % to 0.9 wt. %, or 0.1 wt. % to 0.2 wt. % or to 0.45 wt. %.

Hydraulics Oil, Turbine Oil or Circulating Oil

In one embodiment, the lubricating composition in accordance with the present invention is for use in a hydraulic system, turbine system or a circulating oil system. A hydraulic system is generally a device or apparatus in which a fluid, typically an oil-based fluid, transmits energy to different parts of the system by hydraulic force. A turbine lubricant is typically used to lubricate the gears or other moving parts of a turbine (or turbine system), such as a steam turbine or a gas turbine. A circulating oil is typically used to distribute heat to or through a device or apparatus through which it is circulated.

In one embodiment the lubricant composition contains the polyolefin-substituted bridged hydroxyaromatic compound or salt thereof as described herein in an amount from 0.001 wt % or 0.005 wt % to 5 wt %, or 0.01 wt % or 0.05 wt % to 1.5 wt %, 0.05 wt % to 1 wt %, 0.01 wt % to 1 wt %, 0.01 wt % to 0.5 wt % of the overall composition.

The hydraulic, turbine, or circulating lubricant compositions may also contain one or more additional additives. In some embodiments the additional additives may include an antioxidant, an anti-wear agent, a corrosion inhibitor, a rust inhibitor, a foam inhibitor, a dispersant, a demulsifier, a metal deactivator, a friction modifier, a detergent, other than the polyolefin-substituted bridged hydroxyaromatic compound or metal salt thereof of the present invention, an emulsifier, an extreme pressure agent, a pour point depressant, a viscosity modifier, or any combination thereof.

The lubricant may thus comprise an antioxidant, or mixtures thereof. The anti-oxidant may be present at 0 wt % to 4.0 wt %, or 0.02 wt % to 3.0 wt %, or 0.03 wt % to 1.5 wt % of the lubricant.

Anti-oxidants include diarylamine, alkylated diarylamines, hindered phenols, molybdenum compounds (such as molybdenum dithiocarbamates), ashless dithiocarbamates, hydroxyl thioethers, trimethyl polyquinoline (e.g., 1,2-dihydro-2,2,4-trimethylquinoline), or mixtures thereof.

The diarylamine or alkylated diarylamine may be a phenyl-α-naphthylamine (PANA), an alkylated diphenylamine, or an alkylated phenylnaphthylamine, or mixtures thereof. The alkylated diphenylamine may include di-nonylated diphenylamine, nonyl diphenylamine, octyl diphenylamine, di-octylated diphenylamine, di-decylated diphenylamine, decyl diphenylamine, benzyl diphenylamine and mixtures thereof. In one embodiment the diphenylamine may include nonyl diphenylamine, dinonyl diphenylamine, octyl diphenylamine, dioctyl diphenylamine, or mixtures thereof. In one embodiment the alkylated diphenylamine may include nonyl diphenylamine, or dinonyl diphenylamine. The alkylated diarylamine may include octyl, di-octyl, nonyl, di-nonyl, decyl or di-decyl phenylnapthylamines. In one embodiment, the diphenylamine is alkylated with a benzene and t-butyl substituent.

The hindered phenol antioxidant often contains a secondary butyl and/or a tertiary butyl group as a sterically hindering group. The phenol group may be further substituted with a hydrocarbyl group (typically linear or branched alkyl) and/or a bridging group linking to a second aromatic group. Examples of suitable hindered phenol antioxidants include 2,6-di-tert-butylphenol, 4-methyl-2,6-di-tert-butylphenol, 4-ethyl-2,6-di-tert-butylphenol, 4-propyl-2,6-di-tert-butyl-phenol or 4-butyl-2,6-di-tert-butylphenol, or 4-dodecyl-2,6-di-tert-butylphenol. In one embodiment the hindered phenol antioxidant may be an ester and may include, e.g., Irganox™ L-135 from BASF GmbH. A more detailed description of suitable ester-containing hindered phenol anti-oxidant chemistry is found in U.S. Pat. No. 6,559,105.

Examples of molybdenum dithiocarbamates, which may be used as an antioxidants, include commercial materials sold under the trade names such as Molyvan 822®, Molyvan® A, Molyvan® 855 and from R. T. Vanderbilt Co., Ltd., and Adeka Sakura-Lube™ S100, S165, S600 and S525, or mixtures thereof. An example of an ashless dithiocarbamate which may be used as an anti-oxidant or anti-wear agent is Vanlube® 7723 from R. T. Vanderbilt Co., Ltd.

The antioxidant may include a substituted hydrocarbyl mono-sulfide represented by the formula:

wherein R⁶ may be a saturated or unsaturated branched or linear alkyl group with 8 to 20 carbon atoms; R¹, R⁸, R⁹ and R¹⁰ are independently hydrogen or alkyl containing 1 to 3 carbon atoms. In some embodiments the substituted hydrocarbyl monosulfides include n-dodecyl-2-hydroxyethyl sulfide, 1-(tert-dodecylthio)-2-propanol, or combinations thereof. In some embodiments the substituted hydrocarbyl monosulfide is 1-(tert-dodecylthio)-2-propanol.

The lubricant compositions may also include a dispersant or mixtures thereof. Suitable dispersants include: (i) polyetheramines; (ii) borated succinimide dispersants; (iii) non-borated succinimide dispersants; (iv) Mannich reaction products of a dialkylamine, an aldehyde and a hydrocarbyl substituted phenol; or any combination thereof. In some embodiments the dispersant may be present at 0 wt % or 0.01 wt % to 2.0 wt %, 0.05 wt % to 1.5 wt %, or 0.005 wt % to 1 wt %, or 0.05 wt % to 0.5 wt % of the overall composition.

Dispersants which may be included in the composition include those with an oil soluble polymeric hydrocarbon backbone and having functional groups that are capable of associating with particles to be dispersed. The polymeric hydrocarbon backbone may have a weight average molecular weight ranging from 750 to 1500 Daltons. Exemplary functional groups include amines, alcohols, amides, and ester polar moieties which are attached to the polymer backbone, often via a bridging group. Example dispersants include Mannich dispersants, described in U.S. Pat. Nos. 3,697,574 and 3,736,357; ashless succinimide dispersants described in U.S. Pat. Nos. 4,234,435 and 4,636,322; amine dispersants described in U.S. Pat. Nos. 3,219,666, 3,565,804, and 5,633,326; Koch dispersants, described in U.S. Pat. Nos. 5,936,041, 5,643,859, and 5,627,259, and polyalkylene succinimide dispersants, described in U.S. Pat. Nos. 5,851,965, 5,853,434, and 5,792,729.

In an embodiment, the dispersant can be a “substantially nitrogen free” dispersant. As used herein the term “substantially nitrogen free” means the dispersant contributes about 35 ppm or less, in one embodiment about 25 ppm or less, in another embodiment about 15 ppm or less and in another embodiment about 5 ppm or less nitrogen to the composition. In one embodiment of the invention substantially nitrogen free dispersant is free of nitrogen. The substantially nitrogen free dispersants are prepared by a process described in U.S. Pat. Nos. 3,804,763, 4,031,118 and British Patent Application GB 2,111,256.

In one embodiment, the dispersant can be a polyether represented by the formula R7O[CH2CH(R8)O]qH, where R7 is a hydrocarbyl group, R8 is selected from the group consisting of hydrogen, hydrocarbyl groups of 1 to 16 carbon atoms, and mixtures thereof, and q is a number from 2 to about 50. A commercial example of a polyether is Lyondell ND™ series. Other suitable polyethers are also available from Dow Chemicals, Huntsman, and Akzo.

Anti-foam agents, also known as foam inhibitors, are known in the art and include organic silicones and non-silicon foam inhibitors. Examples of organic silicones include dimethyl silicone and polysiloxanes. Examples of non-silicon foam inhibitors include copolymers of ethyl acrylate and 2-ethylhexylacrylate, terpolymers of ethyl acrylate, 2-ethylhexylacrylate and vinyl acetate, polyethers, polyacrylates and mixtures thereof. In some embodiments the anti-foam is a polyacrylate. Antifoams may be present in the composition from 0.001 wt % to 0.012 wt % or 0.004 wt % or even 0.001 wt % to 0.003 wt %.

Demulsifiers are known in the art and include derivatives of propylene oxide, ethylene oxide, polyoxyalkylene alcohols, alkyl amines, amino alcohols, diamines or polyamines reacted sequentially with ethylene oxide or substituted ethylene oxides or mixtures thereof. Examples of demulsifiers include polyethylene glycols, polyethylene oxides, polypropylene oxides, (ethylene oxide-propylene oxide) polymers and mixtures thereof. In some embodiments the demulsifiers is a polyether. Demulsifiers may be present in the composition from 0.002 wt % to 0.012 wt %.

Pour point depressants are known in the art and include esters of maleic anhydride-styrene copolymers, polymethacrylates; polyacrylates; polyacrylamides; condensation products of haloparaffin waxes and aromatic compounds; vinyl carboxylate polymers; and terpolymers of dialkyl fumarates, vinyl esters of fatty acids, ethylene-vinyl acetate copolymers, alkyl phenol formaldehyde condensation resins, alkyl vinyl ethers and mixtures thereof.

The lubricant composition may also include a rust inhibitor. Suitable rust inhibitors include hydrocarbyl amine salts of alkylphosphoric acid, hydrocarbyl amine salts of dialkyldithiophosphoric acid, hydrocarbyl amine salts of hydrocarbyl aryl sulfonic acid fatty carboxylic acids or esters thereof, an ester of a nitrogen-containing carboxylic acid, an ammonium sulfonate, an imidazoline, alkylated succinic acid derivatives reacted with alcohols or ethers, or any combination thereof; or mixtures thereof.

Suitable hydrocarbyl amine salts of alkylphosphoric acid may be represented by the following formula:

wherein R²⁶ and R²⁷ are independently hydrogen, alkyl chains or hydrocarbyl, typically at least one of R²⁶ and R²⁷ are hydrocarbyl. R²⁶ and R²⁷ contain 4 to 30, or 8 to 25, or 10 to 20, or 13 to 19 carbon atoms. R²⁸, R²⁹ and R³⁰ are independently hydrogen, alkyl branched or linear alkyl chains with 1 to 30, or 4 to 24, or 6 to 20, or 10 to 16 carbon atoms. R²⁸, R²⁹ and R³⁰ are independently hydrogen, alkyl branched or linear alkyl chains, or at least one, or two of R²⁸, R²⁹ and R³⁰ are hydrogen.

Examples of alkyl groups suitable for R²⁸, R²⁹ and R³⁰ include butyl, sec butyl, isobutyl, tert-butyl, pentyl, n-hexyl, sec hexyl, n-octyl, 2-ethyl, hexyl, decyl, undecyl, dodecyl, tridecyl, tetradecyl, pentadecyl, hexadecyl, heptadecyl, octadecyl, octadecenyl, nonadecyl, eicosyl or mixtures thereof.

In one embodiment the hydrocarbyl amine salt of an alkylphosphoric acid is the reaction product of a C₁₄ to C₁₈ alkylated phosphoric acid with Primene® 81 R (produced and sold by Rohm & Haas) which is a mixture of C₁₁ to C₁₄ tertiary alkyl primary amines.

Hydrocarbyl amine salts of dialkyldithiophosphoric acid may include a rust inhibitor such as a hydrocarbyl amine salt of dialkyldithiophosphoric acid. These may be a reaction product of heptyl or octyl or nonyl dithiophosphoric acids with ethylene diamine, morpholine or Primene® 81 R or mixtures thereof.

The hydrocarbyl amine salts of hydrocarbyl aryl sulfonic acid may include ethylene diamine salt of dinonyl naphthalene sulfonic acid.

Examples of suitable fatty carboxylic acids or esters thereof include glycerol monooleate and oleic acid. An example of a suitable ester of a nitrogen-containing carboxylic acid includes oleyl sarcosine.

The rust inhibitors may be present in the range from 0 or 0.02 wt % to 0.2 wt %, from 0.03 wt % to 0.15 wt %, from 0.04 wt % to 0.12 wt %, or from 0.05 wt % to 0.1 wt % of the lubricating oil composition. The rust inhibitors may be used alone or in mixtures thereof.

The lubricant may contain a metal deactivator, or mixtures thereof. Metal deactivators may be chosen from a derivative of benzotriazole (typically tolyltriazole), 1,2,4-triazole, benzimidazole, 2-alkyldithiobenzimidazole or 2-alkyldithiobenzothiazole, 1-amino-2-propanol, a derivative of dimercaptothiadiazole, octylamine octanoate, condensation products of dodecenyl succinic acid or anhydride and/or a fatty acid such as oleic acid with a polyamine. The metal deactivators may also be described as corrosion inhibitors.

The metal deactivators may be present in the range from 0 or 0.001 wt % to 0.1 wt %, from 0.01 wt % to 0.04 wt % or from 0.015 wt % to 0.03 wt % of the lubricating oil composition. Metal deactivators may also be present in the composition from 0.002 wt % or 0.004 wt % to 0.02 wt %. The metal deactivator may be used alone or mixtures thereof.

In one embodiment the invention provides a lubricant composition further comprises a metal-containing detergent, other than the polyolefin-substituted bridged hydroxyaromatic compounds or salts as described herein. The additional metal-containing detergent may include an neutral or overbased, Newtonian or non-Newtonian, basic salts of alkali, alkaline earth and transition metals with one or more a phenate, a sulfurized phenate, a sulfonate, a carboxylic acid, a phosphorus acid, a mono- and/or a di-thiophosphoric acid, saligenin, an alkyl salicylate, a salixarate or mixtures thereof. A neutral detergent has a metal:detergent (soap) equivalence ratio of approximately one. An overbased detergent has a metal:detergent equivalence ratio exceeding one, i.e. the metal content is more than that necessary to provide for a neutral salt of the detergent. The metal-containing detergent may also be an overbased detergent with total base number ranges from 30 to 500 mg KOH/g Equivalents. In one embodiment, the additional metal-containing detergent comprises at least one overbased metal-containing with a metal:detergent ratio of at least 3. The additional metal-containing detergent may have a metal:detergent ratio of at least 5, or at least 8, or at least 12. The additional metal-containing detergent may be borated with a borating agent such as boric acid, e.g., a borated overbased calcium or magnesium sulfonate detergent, or mixtures thereof.

Examples of suitable metal-containing calcium sulfonate detergents include for example calcium dinonyl naphthalene sulfonate, calcium didecyl naphthalene sulfonate, didodecyl naphthalene sulfonate, calcium dipentadecyl naphthalene sulfonate, calcium dinonyl benzene sulfonate, calcium didecyl benzene sulfonate, didodecyl benzene sulfonate, calcium dipentadecyl benzene sulfonate, calcium dihexadecyl benzene sulfonate, calcium diheptadecyl benzene sulfonate, calcium dioctadecyl benzene sulfonate or mixtures thereof. In one embodiment the metal-containing detergent comprises neutral or slightly overbased calcium dinonyl naphthalene sulfonate, or mixtures thereof. The sulfonate detergent may also have corrosion inhibitor properties.

The additional metal-containing detergent may be present at 0 wt % to 5 wt %, or 0.001 wt % to 1.5 wt %, or 0.005 wt % to 1 wt %, or 0.01 wt % to 0.5 wt % of the hydraulic composition.

The lubricant may comprise an extreme pressure agent. The extreme pressure agent may be a compound containing sulfur and/or phosphorus. Examples of extreme pressure agents include polysulfides, sulfurized olefins, thiadiazoles, or mixtures thereof.

Examples of a thiadiazole include 2,5-dimercapto-1,3,4-thiadiazole, or oligomers thereof, a hydrocarbyl-substituted 2,5-dimercapto-1,3,4-thiadiazole, a hydrocarbylthio-substituted 2,5-dimercapto-1,3,4-thiadiazole, or oligomers thereof. The oligomers of hydrocarbyl-substituted 2,5-dimercapto-1,3,4-thiadiazole typically form by forming a sulfur-sulfur bond between 2,5-dimercapto-1,3,4-thiadiazole units to form oligomers of two or more of said thiadiazole units. Examples of a suitable thiadiazole compound include at least one of a dimercaptothiadiazole, 2,5-dimercapto-[1,3,4]-thiadiazole, 3,5-dimercapto-[1,2,4]-thiadiazole, 3,4-dimercapto-[1,2,5]-thiadiazole, or 4-5-dimercapto-[1,2,3]-thiadiazole. Typically readily available materials such as 2,5-dimercapto-1,3,4-thiadiazole or a hydrocarbyl-substituted 2,5-dimercapto-1,3,4-thiadiazole or a hydrocarbylthio-substituted 2,5-dimercapto-1,3,4-thiadiazole are commonly utilized. In different embodiments the number of carbon atoms on the hydrocarbyl-substituent group includes 1 to 30, 2 to 25, 4 to 20, 6 to 16, or 8 to 10. The 2,5-dimercapto-1,3,4-thiadiazole may be 2,5-dioctyl dithio-1,3,4-thiadiazole, or 2,5-dinonyl dithio-1,3,4-thiadiazole.

The polysulfide may include a sulfurized organic polysulfide from oils, fatty acids or esters, olefins, or polyolefins.

Oils which may be sulfurized include natural or synthetic oils such as mineral oils, lard oil, carboxylate esters derived from aliphatic alcohols and fatty acids or aliphatic carboxylic acids (e.g., myristyl oleate and oleyl oleate), and synthetic unsaturated esters or glycerides.

Fatty acids include those that contain 8 to 30, or 12 to 24 carbon atoms. Examples of fatty acids include oleic, linoleic, linolenic, and tall oil. Sulfurized fatty acid esters prepared from mixed unsaturated fatty acid esters such as are obtained from animal fats and vegetable oils, including tall oil, linseed oil, soybean oil, rapeseed oil, and fish oil.

The polysulfide includes olefins derived from a wide range of alkenes. The alkenes typically have one or more double bonds. The olefins in one embodiment contain 3 to 30 carbon atoms. In other embodiments, olefins contain 3 to 16, or 3 to 9 carbon atoms. In one embodiment the sulfurized olefin includes an olefin derived from propylene, isobutylene, pentene or mixtures thereof. In one embodiment the polysulfide comprises a polyolefin derived from polymerizing by known techniques an olefin as described above. In one embodiment the polysulfide includes dibutyl tetrasulfide, sulfurized methyl ester of oleic acid, sulfurized alkylphenol, sulfurized dipentene, sulfurized dicyclopentadiene, sulfurized terpene, and sulfurized Diels-Alder adducts.

The extreme pressure agent may be present at 0 wt % to 3 wt %, 0.005 wt % to 2 wt %, 0.01 wt % to 1.0 wt % of the hydraulics composition.

The lubricant may further comprise a viscosity modifier, or mixtures thereof. Viscosity modifiers (often referred to as viscosity index improvers) suitable for use in the invention include polymeric materials including a styrene-butadiene rubber, an olefin copolymer, a hydrogenated styrene-isoprene polymer, a hydrogenated radical isoprene polymer, a poly(meth)acrylic acid ester, a polyalkylstyrene, an hydrogenated alkenylaryl conjugated-diene copolymer, an ester of maleic anhydride-styrene copolymer or mixtures thereof. In some embodiments the viscosity modifier is a poly(meth)acrylic acid ester, an olefin copolymer or mixtures thereof. The viscosity modifiers may be present at 0 wt % to 10 wt %, 0.5 wt % to 8 wt %, 1 wt % to 6 wt % of the lubricant.

In one embodiment the lubricant disclosed herein may contain at least one friction modifier. The friction modifier may be present at 0 wt % to 3 wt %, or 0.02 wt % to 2 wt %, or 0.05 wt % to 1 wt %, of the lubricant composition.

As used herein the term “fatty alkyl” or “fatty” in relation to friction modifiers means a carbon chain having 10 to 22 carbon atoms, typically a straight carbon chain. Alternatively, the fatty alkyl may be a mono branched alkyl group, with branching typically at the β-position. Examples of mono branched alkyl groups include 2-ethylhexyl, 2-propylheptyl or 2-octyldodecyl.

Examples of suitable friction modifiers include long chain fatty acid derivatives of amines, fatty esters, or fatty epoxides; fatty imidazolines such as condensation products of carboxylic acids and polyalkylene-polyamines; amine salts of alkylphosphoric acids; fatty phosphonates; fatty phosphites; borated phospholipids, borated fatty epoxides; glycerol esters; borated glycerol esters; fatty amines; alkoxylated fatty amines; borated alkoxylated fatty amines; hydroxyl and polyhydroxy fatty amines including tertiary hydroxy fatty amines; hydroxy alkyl amides; metal salts of fatty acids; metal salts of alkyl salicylates; fatty oxazolines; fatty ethoxylated alcohols; condensation products of carboxylic acids and polyalkylene polyamines; or reaction products from fatty carboxylic acids with guanidine, aminoguanidine, urea, or thiourea and salts thereof.

In one embodiment the lubricant composition further includes an anti-wear agent. Typically the anti-wear agent may be a phosphorus anti-wear agent or mixtures thereof. The anti-wear agent may be present at 0 wt % to 5 wt %, 0.001 wt % to 2 wt %, 0.01 wt % to 1.0 wt % of the lubricant.

The phosphorus anti-wear agent may include a phosphorus amine salt, or mixtures thereof. The phosphorus amine salt includes an amine salt of a phosphorus acid ester or mixtures thereof. The amine salt of a phosphorus acid ester includes phosphoric acid esters and amine salts thereof; dialkyldithiophosphoric acid esters and amine salts thereof; phosphites; and amine salts of phosphorus-containing carboxylic esters, ethers, and amides; hydroxy substituted di or tri esters of phosphoric or thiophosphoric acid and amine salts thereof; phosphorylated hydroxy substituted di or tri esters of phosphoric or thiophosphoric acid and amine salts thereof; and mixtures thereof. The amine salt of a phosphorus acid ester may be used alone or in combination.

In one embodiment the oil soluble phosphorus amine salt includes partial amine salt-partial metal salt compounds or mixtures thereof. In one embodiment the phosphorus compound further includes a sulfur atom in the molecule.

Examples of the anti-wear agent may include a non-ionic phosphorus compound (typically compounds having phosphorus atoms with an oxidation state of +3 or +5). In one embodiment the amine salt of the phosphorus compound may be ashless, i.e., metal-free (prior to being mixed with other components).

The amines which may be suitable for use as the amine salt include primary amines, secondary amines, tertiary amines, and mixtures thereof. The amines include those with at least one hydrocarbyl group, or, in certain embodiments, two or three hydrocarbyl groups. The hydrocarbyl groups may contain 2 to 30 carbon atoms, or in other embodiments 8 to 26, or 10 to 20, or 13 to 19 carbon atoms.

Primary amines include ethylamine, propylamine, butylamine, 2-ethylhexylamine, octylamine, and dodecylamine, as well as such fatty amines as n-octylamine, n-decylamine, n-dodecylamine, n-tetradecylamine, n-hexadecylamine, n-octadecylamine and oleyamine. Other useful fatty amines include commercially available fatty amines such as “Armeen®” amines (products available from Akzo Chemicals, Chicago, Ill.), such as Armeen C, Armeen O, Armeen OL, Armeen T, Armeen HT, Armeen S and Armeen SD, wherein the letter designation relates to the fatty group, such as coco, oleyl, tallow, or stearyl groups.

Examples of suitable secondary amines include dimethylamine, diethylamine, dipropylamine, dibutylamine, diamylamine, dihexylamine, diheptylamine, methylethylamine, ethylbutylamine and ethylamylamine. The secondary amines may be cyclic amines such as piperidine, piperazine and morpholine.

The amine may also be a tertiary-aliphatic primary amine. The aliphatic group in this case may be an alkyl group containing 2 to 30, or 6 to 26, or 8 to 24 carbon atoms. Tertiary alkyl amines include monoamines such as tert-butylamine, tert-hexylamine, 1-methyl-1-amino-cyclohexane, tert-octylamine, tert-decylamine, tertdodecylamine, tert-tetradecylamine, tert-hexadecylamine, tert-octadecylamine, tert-tetracosanylamine, and tert-octacosanylamine.

In one embodiment the phosphorus acid amine salt includes an amine with C11 to C14 tertiary alkyl primary groups or mixtures thereof. In one embodiment the phosphorus acid amine salt includes an amine with C14 to C18 tertiary alkyl primary amines or mixtures thereof. In one embodiment the phosphorus acid amine salt includes an amine with C18 to C22 tertiary alkyl primary amines or mixtures thereof. Mixtures of amines may also be used. In one embodiment a useful mixture of amines is “Primene® 81 R” and “Primene® JMT.” Primene® 81 R and Primene® JMT (both produced and sold by Rohm & Haas) are mixtures of C11 to C14 tertiary alkyl primary amines and C18 to C22 tertiary alkyl primary amines respectively.

In one embodiment oil soluble amine salts of phosphorus compounds include a sulfur-free amine salt of a phosphorus-containing compound may be obtained/obtainable by a process comprising: reacting an amine with either (i) a hydroxy-substituted di-ester of phosphoric acid, or (ii) a phosphorylated hydroxy-substituted di- or tri-ester of phosphoric acid. A more detailed description of compounds of this type is disclosed in U.S. Pat. No. 8,361,941.

In one embodiment the hydrocarbyl amine salt of an alkylphosphoric acid ester is the reaction product of a C14 to C18 alkylated phosphoric acid with Primene 81 R® (produced and sold by Rohm & Haas) which is a mixture of C11 to C14 tertiary alkyl primary amines.

Examples of hydrocarbyl amine salts of dialkyldithiophosphoric acid esters include the reaction product(s) of isopropyl, methyl-amyl (4-methyl-2-pentyl or mixtures thereof), 2-ethylhexyl, heptyl, octyl or nonyl dithiophosphoric acids with ethylene diamine, morpholine, or Primene 81 R™, and mixtures thereof.

In one embodiment the dithiophosphoric acid may be reacted with an epoxide or a glycol. This reaction product is further reacted with a phosphorus acid, anhydride, or lower ester. The epoxide includes an aliphatic epoxide or a styrene oxide. Examples of useful epoxides include ethylene oxide, propylene oxide, butene oxide, octene oxide, dodecene oxide, and styrene oxide. In one embodiment the epoxide may be propylene oxide. The glycols may be aliphatic glycols having from 1 to 12, or from 2 to 6, or 2 to 3 carbon atoms. The dithiophosphoric acids, glycols, epoxides, inorganic phosphorus reagents, and methods of reacting the same are described in U.S. Pat. Nos. 3,197,405 and 3,544,465. The resulting acids may then be salted with amines. An example of suitable dithiophosphoric acid is prepared by adding phosphorus pentoxide (about 64 grams) at 58° C. over a period of 45 minutes to 514 grams of hydroxypropyl 0,0′-di(4-methyl-2-pentyl)phosphorodithioate (prepared by reacting di(4-methyl-2-pentyl)-phosphorodithioic acid with 1.3 moles of propylene oxide at 25° C.). The mixture may be heated at 75° C. for 2.5 hours, mixed with a diatomaceous earth and filtered at 70° C. The filtrate contains 11.8% by weight phosphorus, 15.2% by weight sulfur, and an acid number of 87 (bromophenol blue).

In one embodiment the anti-wear additives may include a zinc dialkyldithiophosphate. In other embodiments the compositions of the present invention are substantially free of, or even completely free of zinc dialkyldithiophosphate.

In one embodiment the invention provides for a composition that includes a dithiocarbamate antiwear agent defined in U.S. Pat. No. 4,758,362 column 2, line 35 to column 6, line 11. When present the dithiocarbamate antiwear agent may be present from 0.25 wt %, 0.3 wt %, 0.4 wt % or even 0.5 wt % up to 0.75 wt %, 0.7 wt %, 0.6 wt % or even 0.55 wt % in the overall composition.

A hydraulic lubricant may thus comprise:

0.01 wt % to 2 wt % of the polyolefin-substituted bridged hydroxyaromatic compound or salt thereof as described herein,

0.0001 wt % to 0.15 wt % of a corrosion inhibitor chosen from 2,5-bis(tert-dodecyldithio)-1,3,4-thiadiazole, tolyltriazole, or mixtures thereof, an oil of lubricating viscosity,

0.02 wt % to 3 wt % of antioxidant chosen from aminic or phenolic antioxidants, or mixtures thereof,

0 wt % to 1.5 wt % of a dispersant such as a borated succinimide or a non-borated succinimide dispersant or a substantially nitrogen free dispersants as described herein,

0.001 wt % to 1.5 wt % of a neutral or slightly overbased calcium sulfonate and

0.001 wt % to 2 wt %, or 0.01 wt % to 1 wt % of an anti-wear agent chosen from zinc dialkyldithiophosphate, zinc dialkylphosphate, amine salt of a phosphorus acid ester, or mixtures thereof.

A hydraulic lubricant may thus comprise:

0.01 wt % to 1.5 wt % of the polyolefin-substituted bridged hydroxyaromatic compound or salt thereof as described herein,

0.0001 wt % to 0.15 wt % of a corrosion inhibitor chosen from 2,5-bis(tert-dodecyldithio)-1,3,4-thiadiazole, tolyltriazole, or mixtures thereof,

an oil of lubricating viscosity,

0.02 wt % to 3 wt % of antioxidant chosen from aminic or phenolic antioxidants, or mixtures thereof,

0.005 wt % to 1.5 wt % of a dispersant, such as a borated succinimide or a non-borated succinimide dispersant or a substantially nitrogen free dispersant as described herein,

0.001 wt % to 1.5 wt % of a neutral of slightly overbased calcium sulfonate

0.001 wt % to 2 wt %, or 0.01 wt % to 1 wt % of an anti-wear agent chosen from zinc dialkyldithiophosphate, zinc dialkylphosphate, amine salt of a phosphorus acid ester, or mixtures thereof.

A hydraulic lubricant may also comprise a formulation defined in the following table:

TABLE 3 Hydraulic Lubricant compositions Embodiments (wt %) Additive A B C Polyolefin-substituted bridged 0.01 to 2.0  0.01 to 1.5   0.01 to 1.0  hydroxyaromatic compound or salt thereof as described herein Antioxidant   0 to 4.0 0.02 to 3.0  0.03 to 1.5 Dispersant   0 to 2.0 0.005 to 1.5   0.01 to 1.0 Detergent   0 to 5.0 0.001 to 1.5   0.005 to 1.0  Anti-wear Agent   0 to 5.0 0.001 to 2      0.1 to 1.0 Friction Modifier   0 to 3.0  0.02 to 2    0.05 to 1.0 Viscosity Modifier    0 to 10.0   0.5 to 8.0    1.0 to 6.0 Any Other Performance   0 to 1.3  0.00075 to 0.5      0.001 to 0.4  Additive (antifoam/demulsifier/ pour point depressant) Metal Deactivator   0 to 0.1 0.01 to 0.04 0.015 to 0.03 Rust Inhibitor   0 to 0.2 0.03 to 0.15  0.04 to 0.12 Extreme Pressure Agent   0 to 3.0 0.005 to 2      0.01 to 1.0  Oil of Lubricating Viscosity Balance to Balance to Balance to 100% 100% 100%

Specific examples of a hydraulic lubricant include those summarized in the following table:

TABLE 4 Hydraulic Lubricant compositions Embodiments (wt %) Additive A B C Polyolefin-substituted bridged 0.02 0.06 0.30 hydroxyaromatic compound or salt thereof as described herein Antioxidant-aminic/phenolic 0.4 0.4 0.4 Calcium Sulfonate Detergent 0.02 0.1 0.2 Zinc dialkyl dithiophosphate 0.2 0.5 1.0 Any Other Performance 0.2 0.6 1.0 Additive (antifoam/ demulsifier/pour point depressant) Triazole Metal Deactivator 0.005 0.0075 0.01 Oil of Lubricating Viscosity Balance to Balance to Balance to 100% 100% 100%

The performance of each lubricant may be evaluated in accordance with ASTM D4310-10 (Standard Test Method for Determination of Sludging and Corrosion Tendencies of Inhibited Mineral Oils). Performance is judged by measuring the total amount of sludge formed during the oxidation of lubricants and mineral oil based fluids in the presence of oxygen, water and copper and iron metals at elevated temperatures as well as the ability of these oils to corrode copper catalyst metals.

Without intending to limit the scope of the exemplary embodiment, the following examples illustrate preparation and evaluation of example compounds.

EXAMPLES Example 1: Preparation of Isobutylene-Substituted Phenol

Phenol is alkylated with a 350 Mw high vinylidene polyisobutylene (obtained from Texas Petroleum Products) under standard conditions using boron trifluoride as a catalyst, as shown in reaction scheme 1 above.

Phenol (271.5 g) and toluene (131.2 g) are first mixed in a nitrogen blanketed vessel followed by the dropwise addition of BF₃ phenol complex (43.7 g) over 20 mins. To this mixture, a solution of 350 Mw polyisobutylene (404.3 g, Texas Petroleum Products) diluted in toluene (132.3 g) is added dropwise over 4 hrs. The addition rate is controlled to maintain a temperature between 13-21° C. and never exceeded 28° C.

The reaction mixture is then neutralized slowly with calcium hydroxide (84.0 g) with the temperature being held below 28° C. The neutralized reaction mixture is held for 3 hrs following which diatomaceous earth (100 g) is charged to the reaction and the neutralization completed with ammonia hydroxide (10 g). The reaction mixture is filtered and the filtrate heated under vacuum to a temperature of 185° C. to remove volatiles by distillation. The resulting material is a 350 Mn polyisobutylene-alkylated phenol.

NMR analysis shows the product to be predominately the para-substituted isomer with <3.0% free polyisobutylene present.

Example 2: Bridging of Polyisobutylene-Alkylated Phenol

The material of Example 1 is used to synthesize a neutral calcium phenate using the method shown in scheme 2, above.

The 350 Mw polyisobutylene-alkylated phenol (250.2 g) is heated to 100° C. while stirring in a vessel under a nitrogen blanket. Calcium hydroxide (22.2 g) and ethylene glycol (17.4 g) are added and the mixture is heated to 124° C. Sulfur (45.4 g) is added and the mixture is heated to 185° C. The reaction is held at this temperature for 7 hours. Diluent oil (52.7 g) is added and the mixture is then cooled to room temperature.

Ethylene glycol (13.7 g) and n-decanol (31.9 g) are added to the reaction mixture with stirring, and the mixture is then heated to 168° C. under a nitrogen blanket. Calcium hydroxide (17.3 g) is then added and the mixture is heated to 168° C. while removing volatiles by distillation. Additional diluent oil (39.3 g) is added to the reaction mixture which is heated to 220° C. with vacuum (13 kPa pressure, 27″ Hg vacuum) for 3 hours. The mixture is cooled to 100° C. and then filtered to yield the final product, in diluent oil.

Analysis

Inductively Coupled Plasma (ICP) analysis of the Example 2phenate confirms that the elemental sulfur and calcium contents (measured as wt. % of the product, which includes some diluent in addition to the compound) agree with the theoretical values, as shown in TABLE 2.

TBN is measured according to ASTM D2896 on an oil free basis.

TABLE 2 Analytical Results Wt. % S Wt. % Ca by ICP by ICP TBN Theoretical composition 4.9 5.1 190 Example 2 compound 4.2 5.0 135 Comparative overbased 4.7 5.2 199 calcium phenate

A GPC of the experimental polyisobutylene-substituted calcium phenate shows a number of peaks of increasing molecular weight indicating a number of oligomers including monomers, dimers, trimers, and tetramers, primarily dimers and trimers (i.e., m is 1-2 in Formula 2 above).

Example 3: Preparation of Lubricating Composition

The sulfur bridged calcium phenate of Example 2 is blended into a typical marine diesel cylinder lubricant (MDCL) to provide Example 3.

A comparative MDCL (Example 4) is blended using the commercially available overbased calcium phenate. The compositions of the two lubricant compositions are shown in TABLE 3.

TABLE 3 Exemplary and Baseline Formulations (treat rates are oil free) Example 4 Example 3 Comparative Lubricating Lubricating composition composition Ingredient (% by wt.) (% by wt.) 500N Oil (8-10Cst) Balance to 100% 150BS Oil 29.30 29.0 400TBN Overbased Calcium 8.90 8.9 Sulfonate Borated Succinimide 0.67 0.67 Dispersant Anti-foam agent 0.03 0.03 150TBN Commercial — 3.65 Overbased Calcium Phenate 150TBN Calcium Phenate-350 2.97 — Mw polyisobutylene Phenol

The MDCLs are tested for high temperature deposit forming tendency in both a panel coker apparatus (Similar to GFC Lu-29-T-97).

Panel coker testing is performed as follows: the sample, at 105° C., is splashed for 4 hours on an aluminum panel maintained at 325° C. The aluminum panels are analyzed using image analysis techniques to obtain a universal rating. The rating score is based on 100% being a clean panel and 0% being a panel wholly covered in deposit. Higher values are better, e.g., above 80% is good. The weight of deposit was also determined.

Viscosity at 40° C. and 100° C. are measured according to ASTM D2270-10 (2016), Standard Practice for Calculating Viscosity Index from Kinematic Viscosity at 40° C. and 100° C., and the Viscosity Index (VI) calculated from the results.

The results are shown in TABLE 4, and compared with the baseline marine diesel formulation without the exemplary compound.

TABLE 4 Results Example 4 Example 3 Comparative Lubricating Lubricating Sample composition composition Panel Coker results 55 46 Unit Rating (%) VISCOSITY 232.1 218.9 @40 cSt VISCOSITY 21.05 20 @100 cSt VI 107 105

On the panel coker test, the exemplary 350 Mn polyisobutylene-substituted sulfur bridged phenol calcium salt showed a significant performance boost over the baseline formulation, giving a Unit rating of 55% compared to the baseline of 46%.

The viscosity of the Example 3 lubricating composition was retained well over the temperature range.

Additional bridged polyisobutylene-substituted phenols were prepared in accordance with Examples 4 and 5:

Example 4

The material of Example 1 (400 g) was heated to 100° C. while stirring in a vessel under a nitrogen blanket. Calcium hydroxide (24 g) and ethylene glycol (9 g) were added and the mixture was heated to 124° C. Sulfur (69 g) was added and the mixture was heated to 185° C. The reaction was held at this temperature for 5 hours. Diluent oil (98 g) was added and the mixture was then cooled to room temperature. Ethylene glycol (110 g) and n-decanol (140 g) were added to the reaction mixture with stirring, followed by the addition of alkylbenzene sulfonic acid (34 g) and calcium hydroxide (186 g) and the mixture was then heated to 168° C. under a nitrogen blanket. Carbon dioxide (65 g) was then introduced via subline over 2 hours. Volatile components were then removed by heating the reaction mixture to 220° C., applying vacuum to the system (27″ Hg) and holding for 1 hour. The mixture was cooled to 100° C., with the addition of diluent oil (349 g) and polyisobutylene-substituted succinic anhydride (59.44 g), and then filtered to yield the final product, in diluent oil, which has a oil-free TBN of 396.

Example 5

The material of Example 1 (500 g) was heated to 100° C. while stirring in a vessel under a nitrogen blanket. Calcium hydroxide (44 g) and ethylene glycol (35 g) were added and the mixture was heated to 124° C. Sulfur (91 g) was added and the mixture is heated to 185° C. The reaction was held at this temperature for 7 hours. Diluent oil (103 g) was added and the mixture was then cooled to room temperature. Ethylene glycol (27 g) and n-decanol (64 g) were added to the reaction mixture with stirring, followed by the addition of calcium hydroxide (35 g) and the mixture was then heated to 168° C. under a nitrogen blanket and held for 3 hours. Volatile components were then removed by heating the reaction mixture to 220° C., applying vacuum to the system (27″ Hg) and holding for 1 hour. The mixture was cooled to 100° C., with the addition of diluent oil (113 g) and then filtered to yield the final product, in diluent oil, which has an oil-free TBN of 187.

Additional bridged polyisobutylene-substituted phenols could be made according to Examples 6 and 7:

Example 6

The material of Example 4 (1000 g) is heated to 107° C. while stirring in a vessel under a nitrogen blanket. Calcium hydroxide (306.897 g) is added and stirred for 5 minutes, followed by the addition of acetic acid (11.493 g) while maintaining the temperature below 110° C. The reaction mixture is the heated to 141° C. and stearic acid (276 g) and n-decanol (535 g), followed by increasing the temperature to 154° C. and addition of ethylene glycol (168.00 g). Carbon dioxide (131 g) is then added as fast as possible maintaining the temperature below 168° C. The temperature is reduced to 154° C. and volatiles removed under vacuum (150 mm Hg) and held for 4 hours. The reaction temperature is increased to 220° C. and the vacuum increased to 40 mm Hg. Diluent oil (156 g) and diatomaceous earth (104 g) is added, and then filtered to yield the final product, in diluent oil.

Example 7

The material of Example 1 (555 g) is heated to 100° C. while stirring in a vessel under a nitrogen blanket. Calcium hydroxide (24 g) and ethylene glycol (9 g) are added and the mixture is heated to 124° C. Sulfur (92 g) is added and the mixture is heated to 185° C. The reaction is held at this temperature for 5 hours. Diluent oil (98 g) is added and the mixture is then cooled to room temperature. Ethylene glycol (110 g) and n-decanol (140 g) are added to the reaction mixture with stirring, followed by the addition calcium hydroxide (130 g) and the mixture is then heated to 168° C. under a nitrogen blanket. Carbon dioxide (63 g) is then introduced via subline over 2 hours. Volatile components are then removed by heating the reaction mixture to 220° C., applying vacuum to the system (27″ Hg) and holding for 1 hour. The mixture is cooled to 100° C., with the addition of diluent oil (280 g), and then filtered to yield the final product, in diluent oil.

Each of the documents referred to above is incorporated herein by reference. Except in the Examples, or where otherwise explicitly indicated, all numerical quantities in this description specifying amounts of materials, reaction conditions, molecular weights, number of carbon atoms, and the like, are to be understood as modified by the word “about.” Unless otherwise indicated, each chemical or composition referred to herein should be interpreted as being a commercial grade material which may contain the isomers, by-products, derivatives, and other such materials which are normally understood to be present in the commercial grade. However, the amount of each chemical component is presented exclusive of any solvent or diluent oil, which may be customarily present in the commercial material, unless otherwise indicated. It is to be understood that the upper and lower amount, range, and ratio limits set forth herein may be independently combined. Similarly, the ranges and amounts for each element of the invention may be used together with ranges or amounts for any of the other elements.

The singular forms “a,” “an,” and “the” include plural referents unless the context clearly dictates otherwise.

As used herein, the term “hydrocarbyl substituent” or “hydrocarbyl group” is used in its ordinary sense, which is well-known to those skilled in the art. Specifically, it refers to a group having a carbon atom directly attached to the remainder of the molecule and having predominantly hydrocarbon character. By predominantly hydrocarbon character, it is meant that at least 70% or at least 80% of the atoms in the substituent are hydrogen or carbon. Hydrocarbylene groups are the bivalent equivalents of hydrocarbyl groups, i.e., are attached at each end to two parts of the remainder of the molecule.

Examples of hydrocarbyl groups include:

(i) hydrocarbon substituents, that is, aliphatic (e.g., alkyl or alkenyl), alicyclic (e.g., cycloalkyl, cycloalkenyl) substituents, aryl, and aromatic-, aliphatic-, and alicyclic-substituted aromatic substituents, as well as cyclic substituents wherein the ring is completed through another portion of the molecule (e.g., two substituents together form a ring);

(ii) substituted hydrocarbon substituents, that is, substituents containing non-hydrocarbon groups which, in the context of this invention, do not alter the predominantly hydrocarbon nature of the substituent (e.g., halo (especially chloro and fluoro), hydroxy, alkoxy, mercapto, alkylmercapto, nitro, nitroso, and sulfoxy);

(iii) hetero substituents, that is, substituents which, while having a predominantly hydrocarbon character, may contain other than carbon in a ring or chain otherwise composed of carbon atoms.

Representative alkyl groups useful as hydrocarbyl groups may include at least 1, or at least 2, or at least 3, or at least 4 carbon atoms, and in some embodiments, up to 8, or up to 10, or up to 12, or up to 14, or up to 16, or up to 18 carbon atoms. Illustrative examples include methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, 2-ethylhexyl, nonyl, decyl, undecyl, dodecyl, tridecyl, tetradecyl, hexadecyl, stearyl, icosyl, docosyl, tetracosyl, 2-butyloctyl, 2-butyldecyl, 2-hexyloctyl, 2-hexydecyl, 2-octyldecyl, 2-hexyldodecyl, 2-octyldodecyl, 2-decyltetradecyl, 2-dodecylhexadecyl, 2-hexyldecyloctyldecyl, 2-tetradecyloctyldecyl, 4-methyl-2-pentyl, 2-propylheptyl, monomethyl branched-isostearyl, isomers thereof, mixtures thereof, and the like.

Representative alkenyl groups useful as hydrocarbyl groups include C₂-C₁₈ alkenyl groups, such as ethynyl, 2-propenyl, 1-methylene ethyl, 2-butenyl, 3-butenyl, pentenyl, hexenyl, heptenyl, octenyl, 2-ethylhexenyl, nonenyl, decenyl, undecenyl, dodecenyl, tridecenyl, tetradecenyl, hexadecenyl, isomers thereof, mixtures thereof, and the like.

Representative alicyclic groups useful as hydrocarbyl groups include cyclobutyl, cyclopentyl, and cyclohexyl groups.

Representative aryl groups include phenyl, toluyl, xylyl, cumenyl, mesityl, benzyl, phenethyl, styryl, cinnamyl, benzhydryl, trityl, ethylphenyl, propylphenyl, butylphenyl, pentylphenyl, hexylphenyl, heptylphenyl, octylphenyl, nonylphenyl, decylphenyl, undecylphenyl, dodecylphenyl, benzylphenyl, styrenated phenyl, p-cumylphenyl, α-naphthyl, β-naphthyl groups, and mixtures thereof.

Representative heteroatoms include sulfur, oxygen, nitrogen, and encompass substituents, such as pyridyl, furyl, thienyl and imidazolyl. In general, no more than two, and in one embodiment, no more than one, non-hydrocarbon substituent will be present for every ten carbon atoms in the hydrocarbyl group. In some embodiments, there are no non-hydrocarbon substituents in the hydrocarbyl group.

Numerical values in the specification and claims of this application should be understood to include numerical values which are the same when reduced to the same number of significant figures and numerical values which differ from the stated value by less than the experimental error of conventional measurement technique of the type described in the present application to determine the value.

As used herein, the term “comprising” is inclusive and does not exclude additional, un-recited elements or method steps. However, in each recitation of “comprising” herein, it is intended that the term also encompasses, as alternative embodiments, the phrases “consisting essentially of” and “consisting of,” where “consisting of” excludes any element or steps not specified and “consisting essentially of” permits the inclusion of additional un-recited elements or steps that do not materially affect the basic and novel, and essential characteristics of the composition or method under consideration.

It will be appreciated that variants of the above-disclosed and other features and functions, or alternatives thereof, may be combined into many other different systems or applications. Various presently unforeseen or unanticipated alternatives, modifications, variations or improvements therein may be subsequently made by those skilled in the art which are also intended to be encompassed by the following claims. 

What is claimed is:
 1. A lubricating composition comprising: an oil of lubricating viscosity; a corrosion inhibitor selected from 2,5-bis(tert-dodecyldithio)-1,3,4-thiadiazole, tolyltriazole, or mixtures thereof; an antioxidant selected from aminic or phenolic antioxidants, or mixtures thereof; a dispersant; a neutral of slightly overbased calcium sulfonate; an anti-wear agent selected from zinc dialkyldithiophosphate, zinc dialkylphosphate, amine salt of a phosphorus acid ester, or mixtures thereof; and a compound comprising a polyolefin-substituted bridged hydroxyaromatic compound or salt thereof, wherein the polyolefin is derived from isobutylene having a number average molecular weight of 150 to 400 and wherein the compound is bridged with a sulfide bridge.
 2. (canceled)
 3. (canceled)
 4. (canceled)
 5. The lubricating composition of claim 1, wherein the compound is a metal salt or pnictogen salt.
 6. The lubricating composition of claim 5, wherein the metal in the salt comprises calcium.
 7. The lubricating composition of claim 1, wherein the metal is overbased.
 8. (canceled)
 9. (canceled)
 10. The lubricating composition of claim 1, wherein the compound is a bridged metal phenate.
 11. The lubricating composition of claim 1, wherein the compound is free of C8 and higher unbranched alkyl chains.
 12. The lubricating composition of claim 1, wherein the compound includes a bridged phenate unit represented by the formula:

and salts thereof, where each R1 and each R2 represents an isobutylene group; X represents a sulfide bridging group; Y and Z each represent a terminal group; each n is at least 1; m is at least 1; and p is at least
 1. 13. The lubricating composition of claim 12, wherein the compound is not coupled with cresol.
 14. The lubricating composition of claim 12, wherein n is
 1. 15. (canceled)
 16. (canceled)
 17. The lubricating composition of claim 12, wherein each R1 is a 300-400 MW polyisobutylene.
 18. The lubricating composition of claim 1, wherein the compound has a weight-average molecular weight of 550-5600 in its unsalted form.
 19. The lubricating composition of claim 1, wherein the compound has a weight average molecular weight of up to 2800 in its unsalted form.
 20. The lubricating composition of claim 1, wherein the dispersant comprises a borated succinimide or a non-borated succinimide dispersant or a substantially nitrogen free dispersant as described herein
 21. The lubricating composition of claim 1, wherein the compound is at least 0.01 wt. % of the lubricating composition.
 22. The lubricating composition of claim 20, wherein the compound is at least 0.01 wt % of the lubricating composition.
 23. The lubricating composition of claim 1, wherein the oil of lubricating viscosity comprises at least one of an API Group I, II, III, IV, or V base oil.
 24. The lubricating composition of claim 1, wherein the oil of lubricating viscosity is at least 10 wt. % up to 99.5 wt % of the lubricating composition.
 25. (canceled)
 26. (canceled)
 27. (canceled)
 28. A method of lubricating a hydraulic system, comprising supplying to the hydraulic system a lubricant comprising: 0.0001 wt % to 0.15 wt % of a corrosion inhibitor selected from 2,5-bis(tert-dodecyldithio)-1,3,4-thiadiazole, tolyltriazole, or mixtures thereof, an oil of lubricating viscosity, 0.02 wt % to 3 wt % of antioxidant chosen from aminic or phenolic antioxidants, or mixtures thereof, 0.005 wt % to 1.5 wt % of a dispersant, 0.001 wt % to 1.5 wt % of a neutral or slightly overbased calcium sulphonate, 0.001 wt % to 2 wt % of an antiwear agent chosen from zinc dialkyldithiophosphate, zinc dialkylphosphate, amine salt of a phosphorus acid ester, or mixtures thereof; and 0.001 wt % to 5 wt % of a compound comprising a polyolefin-substituted bridged hydroxyaromatic compound or salt thereof, wherein the polyolefin is derived from isobutylene having a number average molecular weight of 150 to 400 and wherein the compound is bridged with a sulfide bridge.
 29. (canceled)
 30. (canceled)
 31. A method of lubricating a turbine system, comprising supplying to the turbine system a lubricant comprising: 0.0001 wt % to 0.5 wt % of a corrosion inhibitor chosen from 2,5-bis(tert-dodecyldithio)-1,3,4-thiadiazole, tolyltriazole, or mixtures thereof; an oil of lubricating viscosity; 0.01 wt % to 1.5 wt % of antioxidant chosen from aminic or phenolic antioxidants, or mixtures thereof; 0.01 wt % to 2 wt % of a dispersant, 0.001 wt % to 1.5 wt % of a neutral or slightly overbased calcium sulphonate; 0.001 to 1 wt % of a carboxylic acid or anhydride chosen from polyisobutylene succinic acid or anhydride thereof or dodecenyl succinic acid; 0.05 wt % to 1.5 wt % of an antiwear agent chosen from zinc dialkyldithiophosphate, zinc dialkylphosphate, amine salt of a phosphorus acid ester, or mixtures thereof; 0.01 wt % to 1.5 wt % of a compound comprising a polyolefin-substituted bridged hydroxyaromatic compound or salt thereof, wherein the polyolefin is derived from isobutylene having a number average molecular weight of 150 to 400 and wherein the compound is bridged with a sulfide bridge. 